Surface modification of additively manufactured Inconel 718 alloy by low‐energy high‐current electron beam irradiation

Muhammet demirtas,Konstantin V. Ivanov,Gencaga purcek,Harun yanar,Yusuf Kaynak
DOI: https://doi.org/10.1002/adem.202400633
IF: 3.6
2024-06-10
Advanced Engineering Materials
Abstract:The effect of low‐energy high‐current electron beam (LEHCEB) irradiation on the microstructure and nanohardness of Inconel 718 alloy produced by laser powder bed fusion (L‐PBF) additive manufacturing was investigated. The LEHCEB irradiation was applied to the alloy at three energy levels, and resulting microstructural analysis of irradiated surfaces was conducted. The findings from this study demonstrated that the LEHCEB irradiation substantially changed the as‐built microstructure showing intragranular dendrites of different shape and irregular‐shaped Laves phase. The columnar structure formed in the modified near‐surface layer as a result of rapid heating and cooling during LEHCEB irradiation. Furthermore, all Laves phases dissolved in the modified layer. Nanoindentation hardness of irradiated layer of the alloy increased from 593 ± 23 Hv to 693±13 Hv with the highest energy density of 15 J/cm2. This increment was attributed mainly to the dissolution of Laves phases and the formation of an ultrafine columnar structure where the columns were separated from each other by the district regions containing very thin interlayers of a secondary phase and a high amount of dislocations. This article is protected by copyright. All rights reserved.
materials science, multidisciplinary
What problem does this paper attempt to address?