Effects of Laser Annealing on Microstructures and Hardness of Inconel 718

Liufa Liu,Chen Lu,Chunquan Zhai,Wenjiang Ding,Hirose Akio,F.Kobayashi Kojiro

DOI: https://doi.org/10.3321/j.issn:1002-185X.2005.03.042

2005-01-01

Rare Metal Materials and Engineering

Abstract:It was studied annealing on the microstructures and hardness of aged Inconel 718. A 2.5 kW CO2 laser was employed to irradiate the samples surface. Surface layers were heated to high temperatures by laser energy, and then air-cooled. By controlling laser process parameters, hardness in a surface layer can be decreased to that of the standard annealed alloy without surface melting. Microstructures studies suggest that the matrix-strengthening phases (gamma" and gamma') in the surface layer were dissolved by laser irradiation. No changes were observed about other secondary phases. The changes of the precipitation states of these precipitates are proposed as the origination of the hardness decrease. Applicable process parameter ranges defined by defocusing distances and scanning velocities of the laser were established under the same experimental conditions.