Microstructure, Mechanical Property and Heat Treatment Schedule of the Inconel 718 Manufactured by Low and High Power Laser Powder Bed Fusion

Huihui Yang,Zemin Wang,Hongze Wang,Yi Wu,Haowei Wang

DOI: https://doi.org/10.1016/j.msea.2022.144517

IF: 6.044

2022-01-01

Materials Science and Engineering A

Abstract:In this work, the microstructure, mechanical property, and heat treatment schedule of the Inconel 718 alloy manufactured by low and high power laser powder bed fusion (LPBF) were investigated. It was found that the size of the gamma-dendrite and the width of the Laves phase increase gradually but the number of the strengthening phase does not increase obviously as the laser volumetric energy density increases. The tensile strength of the LPBFed Inconel 718 samples reaches its highest value with the ultimate tensile strength of 1087 MPa and yield strength of 834.7 MPa, which exceeds the casting standard of the Inconel 718 alloy. The phase transition dy-namics of the LPBFed Inconel 718 samples under different laser volumetric energy densities are inconsistent during the complete solid solution process. When the solid solution time is 1h, the solid solution temperature of the LPBFed Inconel 718 sample (at 89.28 J/mm3) with a large width of the Laves phase (-750 nm) is 1120 degrees C, which is larger than that (1060 degrees C) of the sample (at 78.13 J/mm3) with a small width of the Laves phase (-150 nm). The solid solution time (t, h) and temperature (T0, degrees C) of the LPBFed Inconel 718 sample with the Laves ) phase width of-750 nm and-150 nm satisfy the following equation: t = 0.24 x 10-5 exp (13715.07and t = T0 ) 0.36 x 10-5 exp (13715.07 , respectively. The tensile strength, yield strength and elongation of the two groups of T0 the LPBFed Inconel 718 samples can reach 1507.07 MPa, 1398.17 MPa, 15.23% and 1531.18 MPa, 1356.02 MPa, 17%, respectively, which greatly exceeds the forging standard of the Inconel 718 alloy.