Preparation and properties of a porous ZrO 2 /SiZrBOC ceramic matrix composite with high temperature resistance and low thermal conductivity

Wanying Zhang,Fengyue Shi,Jianwen Wang,Yang Yang,Guangdong Zhao,Dongyu Zhao

DOI: https://doi.org/10.1016/j.jeurceramsoc.2023.11.007

IF: 5.7

2023-12-18

Journal of the European Ceramic Society

Abstract:In this study, porous ZrO 2 /SiZrBOC and SiZrBOC ceramic matrix composites were produced via vacuum impregnation method, using SiZrBOC ceramic precursor as a matrix, ZrO 2 fiber prepared via electrospinning as the reinforcing agent and polyurethane foam as a skeleton. Polyurethane foam with open porosity is rather a substrate for the creation of a skeletal 3D structure. The preparation process and pyrolysis mechanism of ZrO 2 /SiZrBOC polyurethane foam impregnated with a precursor solution were expounded. The thermal conductivity tests and mechanical property measurements show that the lowest thermal conductivity (0.0378 W m −1 K −1 ) was achieved in the ZrO 2 /SiZrBOC ceramic matrix composite at the pyrolysis temperature of 800 °C, being much inferior to that of the SiZrBOC composite (0.0861 W m −1 K −1 ). At 1400 °C, the maximum compressive strength of the porous ZrO 2 /SiZrBOC ceramic matrix composites reached a value of 1.37 MPa, while that of the SiZrBOC composites was 0.22 MPa only. Therefore, the addition of ZrO 2 fibers improved the compressive strength and thermal insulation properties of the composites.

materials science, ceramics

What problem does this paper attempt to address?

This paper mainly discusses the preparation of a high-temperature resistant and low thermal conductivity porous ZrO2/SiZrBOC ceramic matrix composite. In the study, the composite material was manufactured by vacuum impregnation method, using SiZrBOC ceramic precursor as the matrix, ZrO2 fibers fabricated by electrospinning as the reinforcement, and polyurethane foam as the skeleton. The experimental results show that the ZrO2/SiZrBOC composite material obtained at 800℃ has the lowest thermal conductivity (0.0378 W m-1 K-1), much lower than that of SiZrBOC composite material, and exhibits the maximum compressive strength (1.37 MPa) at 1400℃. Therefore, the addition of ZrO2 fibers significantly improves the compressive strength and thermal insulation performance of the composite material. In addition, these composite materials have potential applications in thermal protection in extreme environments such as aerospace and fire protection systems, as they combine high strength, high temperature resistance, and good insulation effects. The paper also provides detailed descriptions of the material preparation process, chemical composition, crystal behavior, microstructure, mechanical properties, and oxidation resistance.