Abstract:A mixture of the mechanically alloyed 2Si-B-3C-N powder and short carbon fiber was hot pressed at 1800 degrees C for 30 mins in nitrogen. Careful investigation to the prepared C-fiber/2Si-B-3C-N ceramic matrix composite revealed that the composite was very difficult to be densified. Heterogeneous nucleation, abnormal grain growth and severe interface reaction occurred on the fiber surface or between the fiber and the ceramic matrix, leading to a small density and weak mechanical properties of the composite. For the prepared composite without any additive, the relative density, flexural strength, elastic modulus and fracture toughness is 71.7%, 64.6 MPa, 14.7 GPa and 1.47 MPa.m(1/2), respectively. The average size of the SiC grains close to and far away from the carbon fiber is 249.10 nm and 50.45 nm, respectively. However, with the addition of ZrO2 (7.5 mol%), the above mentioned phenomenons are changed noticeably, and those properties are significantly increased to 88.5%, 112.4 MPa, 111.1 GPa and 2.94 MPa.m(1/2), respectively. At the same time, the SiC grains close to or far away from the carbon fiber almost have the same average size of about 448.21 nm, and almost no interface reaction occurs. It shows that the addition of ZrO2 not only facilitates the sintering and densification process, but also depresses the interface reaction, promotes the homogeneous nucleation and grain growth, and hence significantly improves the mechanical properties of the C-fiber/2Si-B-3C-N composite. This interesting finding is favorable for the preparation of carbon fiber reinforced ceramic matrix composite, which requires both a large relative density and well controlled interface reaction.

Preparation and properties of ZrP2O7 matrix composites with high silica fibers reinforcement

Preparation and properties of a porous ZrO 2 /SiZrBOC ceramic matrix composite with high temperature resistance and low thermal conductivity

Preparation and Mechanical Properties of Fine Grain Al2O3-ZrO2 Composite Ceramics

Preparation and Mechanical Properties of ZrO2-reinforced Polymer-Derived SiCNO Composite Ceramics

Mechanical Property of SiC Whisker Reinforced CaZr4(PO4)6 Ceramics Fabricated by Fast Hot Pressure Sintering

Mechanical Properties of Short Carbon Fiber Reinforced ZrB2–SiC Ceramic Matrix Composites

PREPARATION AND PROPERTIES OF SiC_(p1)/ZrB_2 ULTRA-HIGH TEMPERATURE CERAMICS

Preparation and Properties of C/C−ZrB2−SiC Composites by High-Solid-loading Slurry Impregnation and Polymer Infiltration and Pyrolysis (PIP)

Fabrication and Properties of Short Carbon Fiber-ZrB2 Ceramic Matrix Composites

Processing, microstructure, and mechanical properties of chopped SiC fibers reinforced ZrB2–hBN–based composites

Pressureless Sintering of Silicon Carbide Ceramics Containing Zirconium Diboride

Mechanical Properties and In-Situ Toughening Mechanism of Pressurelessly Densified ZrB2–TiB2 Ceramic Composites

Characterization of hot-pressed short carbon fiber reinforced ZrB2–SiC ultra-high temperature ceramic composites

Densification, microstructure and mechanical properties of ZrB2–SiCw ceramic composites

Research on the Interfacial Structure and Property Improvement of the Cfiber/2Si-B-3C-N Ceramic Matrix Composite

Study on Zrc-20vol.%Sicw Ultrahigh Temperature Ceramics by Hot Pressing

Thermal and mechanical properties of porous Y-PSZ/zircon composites

Characterization and mechanical properties of Cf/ZrB2-SiC composites fabricated by a hybrid technique based on slurry impregnation, polymer infiltration and pyrolysis and low-temperature hot pressing

Preparation and Mechanical Properties of Al2O3–15wt.%ZrO2 Composites

Effect of ZrO 2 contents on the mechanical and thermal shock properties of ZrO 2p(3Y)/BN-SiO 2 ceramics composite

Effect of Pyrolytic Carbon Coating on the Microstructure and Fracture Behavior of the Cf/ZrB2-SiC Composite