Ana Carla S. L. S. Coutinho,Joana M. F. Barros,Marcio D. S. Araujo,Jilliano B. Silva,Marcelo J. B. Souza,Regina C. O. B. Delgado,Valter J. Fernandes Jr.,Antonio S. Araujo
Abstract:Heterogeneous catalysts containing cobalt and molybdenum supported on mesoporous materials types SBA-15 and AlSBA-15 were synthesized for application in the HDS reactions of thiophene in the n-heptane stream. The materials were synthesized by the hydrothermal method using Pluronic P123 as a template. The calcined SBA-15 and AlSBA-15 supports were submitted to co-impregnation with solutions of cobalt nitrate and ammonium heptamolybdate, aiming for the production of 15% in mass of metal loading with an atomic ratio of [Co/(Co + Mo)] = 0.45. The obtained materials were dried and calcined to obtain the mesoporous catalysts in the forms of CoMo/SBA-15 and CoMo/AlSBA-15. The catalysts were characterized by XRD, TG/DTG, SEM, and nitrogen adsorption. From XRD analysis, it was verified that after the decomposition of the cobalt and molybdenum salts, MoO3, Co3O4, and CoMoO4 oxides were formed on the supports, being attributed to these chemical species, the activity for the HDS reactions. The catalytic activity of the obtained catalysts was evaluated in a continuously flowing tubular fixed-bed microreactor coupled on-line to a gas chromatograph, using an n-heptane stream containing 12,070 ppm of thiophene (ca. 5100 ppm of sulfur) as a model compound. The synthesized catalysts presented suitable activity for the HDS reaction, and the main obtained products were cis- and trans-2-butene, 1-butene, n-butane, and low amounts of isobutane. The presence of 1,3-butadiene and tetrahydrothiophene (THT) was not detected. A mechanism of the primary and secondary reactions and subsequent formation of the olefins and paraffins in the CoMo/SBA-15 and CoMo/AlSBA-15 mesoporous catalysts was proposed, considering steps of desulfurization, hydrogenation, dehydrogenation, THT decyclization, and isomerization.
What problem does this paper attempt to address?
The problem that this paper attempts to solve is to develop efficient desulfurization catalysts to remove sulfur compounds, especially thiophene, in petroleum fractions. Specifically, the researchers synthesized a series of catalysts based on SBA - 15 and AlSBA - 15 mesoporous materials supported with cobalt - molybdenum oxides, and evaluated the catalytic activity of these catalysts for the hydrodesulfurization (HDS) reaction of thiophene in an n - heptane stream. The main purpose of the study is to improve the activity, selectivity, and stability of the catalysts in the desulfurization process by optimizing their structure and composition, thereby meeting the increasingly stringent environmental protection regulations.
### Background and Objectives of the Paper
1. **Background**:
- Desulfurization is one of the very important steps in the petroleum refining process, mainly achieved through hydrodesulfurization (HDS).
- Currently, the HDS catalysts in use are mainly based on Co(Ni)Mo/Al₂O₃ catalysts, but these catalysts have limitations in the production of ultra - low - sulfur fuels.
- In order to improve the performance of HDS, researchers have explored a variety of new catalysts, including those based on mesoporous materials.
2. **Objectives**:
- Synthesize catalysts based on SBA - 15 and AlSBA - 15 mesoporous materials supported with cobalt - molybdenum oxides.
- Evaluate the catalytic activity of these catalysts for the HDS reaction of thiophene in an n - heptane stream.
- Through experimental and theoretical analysis, understand the mechanism of action of these catalysts in the HDS reaction, thereby providing a theoretical basis for the development of more efficient and environmentally friendly desulfurization catalysts.
### Main Research Contents
1. **Catalyst Synthesis**:
- SBA - 15 and AlSBA - 15 mesoporous materials were synthesized using the hydrothermal method.
- Cobalt nitrate and ammonium heptamolybdate solutions were loaded onto SBA - 15 and AlSBA - 15 by the co - impregnation method to prepare catalysts with a 15% mass fraction of metal loading and an atomic ratio of [Co/(Co + Mo)] = 0.45.
2. **Catalyst Characterization**:
- The catalysts were characterized by means of X - ray diffraction (XRD), thermogravimetry/differential thermogravimetry (TG/DTG), scanning electron microscopy (SEM), and nitrogen adsorption.
- The XRD results showed that after the decomposition of cobalt and molybdenum salts, oxides such as MoO₃, Co₃O₄, and CoMoO₄ were formed, and these chemical species are considered to be the active centers for the HDS reaction.
3. **Catalytic Activity Evaluation**:
- In a continuous - flow fixed - bed microreactor, an n - heptane stream containing 12,070 ppm thiophene (about 5,100 ppm sulfur) was used as a model compound to evaluate the catalytic activity of the catalysts.
- The experimental results showed that the synthesized catalysts had good HDS activity, and the main products were cis - and trans - 2 - butene, 1 - butene, n - butane, and a small amount of isobutane. 1,3 - Butadiene and tetrahydrothiophene (THT) were not detected.
4. **Reaction Mechanism**:
- The main and secondary reaction mechanisms of the HDS reaction were proposed, including steps such as desulfurization, hydrogenation, dehydrogenation, THT ring - opening, and isomerization.
### Conclusion
This study successfully synthesized catalysts based on SBA - 15 and AlSBA - 15 mesoporous materials supported with cobalt - molybdenum oxides, and proved that these catalysts have good catalytic activity in the HDS reaction. Through detailed experiments and characterizations, the researchers revealed the structural characteristics and reaction mechanisms of these catalysts, providing an important reference for the development of more efficient desulfurization catalysts.