Abstract:The electrical properties of the active precursor ions play an important role in the microstructure of the hydrodesulfurization (HDS) catalyst. Herein, this study first presents a simple strategy to adjust the charge of Mo-based nanoparticles (Mo-NPs) by changing the content of the organic complexing agent dodecyltrimethylammonium bromide (DTAB) and then investigates the effects of Mo-NPs with different charges on HDS catalysts. The results show that the zeta (zeta) potential of the Mo-NPs mutates from negative to positive with the DTA+/Mo molar ratio increasing to 4/7. Compared with conventional electronegative Mo precursors, the electropositive Mo-NPs could eliminate the electrostatic difference with the promoter nickel ions (Ni2+); thus, the Mo-NPs and Ni2+ could synchronously diffuse and co-load into the electropositive pore of gamma-Al2O3 by hydrothermal deposition, resulting in a more uniform distribution of active species (standard deviation of slab length = 0.51 vs. 1.05). Meanwhile, the isolating effect of amorphous carbonaceous species from the thermal decomposition of the organic complexing agent on the active phases was directly observed, and the stabilizer role was powerfully verified. Therefore, the resultant catalyst not only realized better Ni-promoted effects (synergetic factor = 7.5 vs. 5.3) but also exhibited excellent active phase morphology with much shorter length, higher stacking number and better dispersion. Finally, compared with the catalyst prepared from the conventional precursor, i.e. Mo7O246-, the Mo-NPs-derived catalyst shows the more excellent HDS activity of dibenzothiophene (reaction rate constant kHDS = 7.51 vs. 1.06 x 10-7 mol g-1 s-1; turnover frequency TOF = 5.56 vs. 1.43 h-1) and obviously enhanced HDS ratio of heavy coking diesel (99.8% vs. 96.2%). Besides, the resulting catalyst also holds a much higher HDS ratio as compared with the industrial catalyst (99.8% vs. 97.8%), showing a great potential in industrial application. The present work sheds light on the rational design of supported nanosized catalysts and provides a deeper understanding of the complicated structure-function relations. Using electropositive Mo-based nanoparticles (Mo-NPs) as precursor could realize the resulting catalyst with more uniform, shorter, higher layered, better Ni-promoted, and stable MoS2 slabs, thus holding excellent HDS performance.

Mesoporous Carbon Supported Co-Mo and Ni-Mo Catalysts for Hydrodesulfurization

Synthesis of Novel NiMo Catalysts Supported on Highly Ordered TiO2-Al2O3 Composites and Their Superior Catalytic Performance for 4,6-Dimethyldibenzothiophene Hydrodesulfurization

Synthesis of NiMo Catalysts Supported on Gallium-Containing Mesoporous Y Zeolites with Different Gallium Contents and Their High Activities in the Hydrodesulfurization of 4,6-Dimethyldibenzothiophene

Comparative Study on Molybdenum Nitride, Phosphide and Carbide

Catalytic Characteristics of Active Corner Sites in CoMoS Nanostructure Hydrodesulfurization – A Mechanism Study Based on DFT Calculations

Hydrodesulfurization of 4,6-dimethyldibenzothiophene over NiMo sulfide catalysts supported on meso-microporous Y zeolite with different mesopore sizes

Role of the Solvent Evaporating Temperature on the NiMo/TiO2-Al2O3 Catalyst and the Hydrodesulfurization Performance for 4,6-Dimenthyldibenzothiophehe

Synthesis of alumina-nitrogen-doped carbon support for CoMo catalysts in hydrodesulfurization process

Electronic structure regulation of CoMoS catalysts by N, P co-doped carbon modification for effective hydrodesulfurization

States of Carbon Nanotube Supported Mo-Based HDS Catalysts

Construction of High Content CoMoS Active Sites Through the Combination of Co 5 Mo 10 Molecular Precursors and Inert Carbon Matrix Support for Deep Hydrodesulfurization

Bimodal mesoporous AlMCM-41 supported NiMo catalysts for efficient hydrodesulfurization of 4,6-dimethyldibenzothiophene

Design And Synthesis Of Metal Sulfide Catalysts Supported On Zeolite Nanofiber Bundles With Unprecedented Hydrodesulfurization Activities

Hydroisomerization of Model FCC Naphtha over Sulfided Co(Ni)–Mo(W)/MCM-41 Catalysts

A novel and facile strategy for the preparation of highly reactive NiMo/γ-Al 2 O 3 hydrodesulfurization catalyst

Effect of Hierarchically Macro-Mesoporous Structure of NiMoS/Al2O3 Catalysts on Hydrodesulfurization Activity

Fabrication of Well-Structured NiMo Hydrodesulfurization Catalysts Using Electropositive Mo-based Nanoparticles

Preparation of Hydrodesulfurization Catalysts Using MoS3 Nanoparticles As a Precursor

Preparation of Co-Mo/γ-Al2O3 catalyst and the catalytic hydrogenation effects on coal-related model compounds

Synthesis of cube MgO@AC and catalytic performance of its supported CoMo for hydrodesulfurization of 4,6-dimethyldibenzothiophene

Hydroisomerization of Model Naphtha over Sulfided Co-Mo/SBA-15 Catalyst