Abstract:The sole micropores strictly restrict the wide utilization of TS-1 zeolite in the catalytic fields, especially in the catalytic conversion of compounds with large molecular sizes. Here, we report a feasible and economical method to overcome this drawback. In this work, the hierarchical TS-1 zeolite was constructed via post-acid treatment, post-alkali etching, and a combination of post-acid treatment and alkali etching methods, after which, the corresponding NiMo-supported catalysts were prepared via the incipient wetness impregnation method. Then, the aforementioned materials were fully characterized using X-ray diffraction (XRD), N-2 adsorption-desorption, pyridine adsorbed Fourier transform infrared spectroscopy (Py - FTIR), H-2 temperature programmed reduction (H-2 - TPR), X-ray photoelectron spectroscopy (XPS), and high-resolution transition electron microscope (HR-TEM) to unravel the changes in the physicochemical properties caused by the post treatments. Finally, the hydrodesulfurization of dibenzothiophene (DBT) was used as a probe to assess the effects of the post-treatments on the catalytic performance of the hierarchical NiMo/TS-1 catalysts. The results showed that the MFI topology of TS-1 zeolite remained undamaged significantly and the serial hierarchical TS-1 zeolites exhibited higher specific surface areas and mesopore structures. Moreover, appropriate amounts of Bronsted acid sites were formed at the surface of the serial hierarchical TS-1 zeolites. The interaction between the active metals and the support materials was also modulated by the post-treatment of TS-1 zeolite, which resulted in better dispersion of Ni promoted MoS2 slabs with a higher proportion of NiMoS active phase, further leading to the enhanced catalytic activity and direct desulfurization pathway selectivity of the corresponding serial hierarchical NiMo/TS-1 catalysts. Among all the prepared catalysts, the catalytic activity was enhanced by approximately 1.2 times over catalyst NiMo/AT-TS-1 obtained by post-acid treatment compared to that over catalyst NiMo/TS-1 without treatment and on which the selectivity of the DDS pathway was 22% higher compared to that over catalyst NiMo/TS-1.

Synthesis, characterization, and performance evaluation of unsupported tetrametallic CoMoMnAl and CoMoZnAl catalysts for selective hydrodesulfurization (HDS)

Synthesis of Novel NiMo Catalysts Supported on Highly Ordered TiO2-Al2O3 Composites and Their Superior Catalytic Performance for 4,6-Dimethyldibenzothiophene Hydrodesulfurization

Synthesis of NiMo Catalysts Supported on Gallium-Containing Mesoporous Y Zeolites with Different Gallium Contents and Their High Activities in the Hydrodesulfurization of 4,6-Dimethyldibenzothiophene

Role of the Solvent Evaporating Temperature on the NiMo/TiO2-Al2O3 Catalyst and the Hydrodesulfurization Performance for 4,6-Dimenthyldibenzothiophehe

Hydrodesulfurization of 4,6-dimethyldibenzothiophene over NiMo sulfide catalysts supported on meso-microporous Y zeolite with different mesopore sizes

Catalytic Characteristics of Active Corner Sites in CoMoS Nanostructure Hydrodesulfurization – A Mechanism Study Based on DFT Calculations

Hydrodesulfurization of Thiophene in n-Heptane Stream Using CoMo/SBA-15 and CoMo/AlSBA-15 Mesoporous Catalysts

Hierarchical TS-1 zeolite loaded with NiMo catalysts: Preparation and performance in hydrodesulfurization

Metal oxides complexes as precursors of sulfide catalysts for HDS of DBT

Construction of High Content CoMoS Active Sites Through the Combination of Co 5 Mo 10 Molecular Precursors and Inert Carbon Matrix Support for Deep Hydrodesulfurization

Influence of Active Phase Structure of CoMo/Al2O3 Catalyst on the Selectivity of Hydrodesulfurization and Hydrodearomatization

Enhanced hydrodesulfurization activity of thiophene over hollow tubular CoMo unsupported catalysts

N-octyltrimethylammonium bromide-assisted self-assembly of CoMo precursors to prepare CoMoS/Al 2 O 3 catalysts for highly selective hydrodesulfurization of thiophene

Synthesis and Characterization of NiMoS/TiMg and NiWS/TiMg Nanocatalysts and Their Application in the Hydrodesulfurization of Dibenzothiophene

Mesoporous Carbon Supported Co-Mo and Ni-Mo Catalysts for Hydrodesulfurization

Electronic structure regulation of CoMoS catalysts by N, P co-doped carbon modification for effective hydrodesulfurization

Hydrodesulfurization of Dibenzothiophene over Ni-Mo-W Sulfide Catalysts Supported on Sol-Gel Al2O3-CeO2

Design And Synthesis Of Metal Sulfide Catalysts Supported On Zeolite Nanofiber Bundles With Unprecedented Hydrodesulfurization Activities

Precise Tuning the CoMoOx/Al2O3 and CoMoSx/Al2O3 Interfacial Structures for Efficient Hydrodesulfurization of Dibenzothiophene

Synthesis of cube MgO@AC and catalytic performance of its supported CoMo for hydrodesulfurization of 4,6-dimethyldibenzothiophene

Sulfured NiMo catalysts on TiO2-Nb2O5 nanocomposites for efficient hydrodesulfurization performance