Abstract:In this paper, Fe-3%Si ultra-thin ribbons prepared by the planar flow casting (PFC) technique were subjected to temper rolling and annealing treatments. The microstructure and texture evolution during this process were examined through experimental measurements coupled with crystal plasticity finite element (CPFE) simulation to assess the feasibility of preparing ultra-thin non-oriented silicon steel using PFC ribbons. The results indicate that the PFC ribbons exhibit a significant columnar crystal structure, and {001}-oriented grains comprise over 30%. After being annealed, the grains with different orientations grew uniformly, the texture components were basically unchanged, and the {001} texture was well preserved. When annealing was carried out after temper rolling with a reduction rate of 7%, uneven grain growth was observed, and the growth tendency of the {001} grains, especially, surpassed that of the {111} grains, with an elevated temperature which peaked at 950 °C, where the proportion of {001} grains was maximal. When being annealed after temper rolling to 15%, grains of other orientations showed significant growth at each temperature, while the {001} grains did not show an obvious growth advantage. Utilizing the CPFE, the deformation-stored energy distribution of each characteristic-oriented grain was simulated, and it was shown that compared to the 15% rolling reduction rate, the deformation-stored energy accumulation of {001}-oriented grains after being rolled to 7% reduction was significantly lower than that of {111}-oriented grains. It suggests that the larger stored energy difference makes {001} grains show a stronger growth advantage based on the SIBM mechanism during annealing, after being rolled with a reduction rate of 7%. Overall, for the synergistic optimization of microstructure and texture, rolling with a 7% reduction rate followed by annealing at 950 °C in a hydrogen atmosphere is most advantageous.

Effect of wheel speed on the microstructure and magnetic properties of Fe-3.0 wt %Si non-oriented silicon steel ultra-thin ribbons prepared by planar flow casting

Numerical modeling investigation of Planar Flow Casting for Fe-6.5wt%Si alloy

Study on Microstructure and Texture of Fe-3%Si Ultra-Thin Ribbons Prepared by Planar Flow Casting

Effect of Grain Size Before Cold Rolling on Microstructure, Texture and Magnetic Properties of Ultra-Thin Low-Si Non-oriented Silicon Steel

Effects of rolling temperature on microstructure, texture, formability and magnetic properties in strip casting Fe-6.5wt% Si non-oriented electrical steel

Effect of recrystallization annealing temperature on microstructure, texture and magnetic properties of non-oriented silicon steel produced by strip casting

Influence Mechanisms of Cold Rolling Reduction Rate on Microstructure, Texture and Magnetic Properties of Non-Oriented Silicon Steel

Effects of Solidification Cooling Rates on Microstructures and Physical Properties of Fe-6.5%Si Alloys

Reducing the Core Losses of Fe-Si-B Amorphous Alloy Ribbons by High Cooling Rate Planar Flow Casting

Microstructure and texture evolution of thin-gauge non-oriented silicon steel with high permeability produced by twin-roll strip casting

Microstructural evolution and magnetic properties in strip cast non-oriented silicon steel produced by warm rolling

Phase Composition, Microstructures and Magnetic Properties of Melt-Spun Nd1.2Fe10.5Mo1.5 Ribbons and Their Nitrides

Effect of wheel speed and subsequent annealing on the microstructure and magnetic properties of nanocomposite Pr2Fe14B/α-Fe magnets

Effect of rolling process on magnetic properties of Fe-3.3 wt% Si non-oriented electrical steel

Effect of Cold Rolling Process on Microstructure, Texture and Properties of Strip Cast Fe-2.6%Si Steel

On the Cooling Rate of Strip Cast Ingots for Sintered NdFeB Magnets

Effect of Cooling Rate on the Microstructure Evolution and Mechanical Properties of Iron-Rich Al–Si Alloy

EFFECT OF COLD ROLLING PROCESS ON TEXTURE EVOLUTION OF GRADIENT MICROSTRUCTURE IN Fe-3,0 % Si NON-ORIENTED SILICON STEEL

Ultra‐Thin 3.5%Si Steel with Both Magnetic Properties and Mechanical Properties Produced by Different Process Routes of Large‐Scale Production

Development of thin-gauge low iron loss non-oriented silicon steel

Effects of Warm Temper Rolling on Microstructure, Texture and Magnetic Properties of Strip-Casting 6.5wt% Si Electrical Steel