Abstract:In this paper, Fe-3%Si ultra-thin ribbons prepared by the planar flow casting (PFC) technique were subjected to temper rolling and annealing treatments. The microstructure and texture evolution during this process were examined through experimental measurements coupled with crystal plasticity finite element (CPFE) simulation to assess the feasibility of preparing ultra-thin non-oriented silicon steel using PFC ribbons. The results indicate that the PFC ribbons exhibit a significant columnar crystal structure, and {001}-oriented grains comprise over 30%. After being annealed, the grains with different orientations grew uniformly, the texture components were basically unchanged, and the {001} texture was well preserved. When annealing was carried out after temper rolling with a reduction rate of 7%, uneven grain growth was observed, and the growth tendency of the {001} grains, especially, surpassed that of the {111} grains, with an elevated temperature which peaked at 950 °C, where the proportion of {001} grains was maximal. When being annealed after temper rolling to 15%, grains of other orientations showed significant growth at each temperature, while the {001} grains did not show an obvious growth advantage. Utilizing the CPFE, the deformation-stored energy distribution of each characteristic-oriented grain was simulated, and it was shown that compared to the 15% rolling reduction rate, the deformation-stored energy accumulation of {001}-oriented grains after being rolled to 7% reduction was significantly lower than that of {111}-oriented grains. It suggests that the larger stored energy difference makes {001} grains show a stronger growth advantage based on the SIBM mechanism during annealing, after being rolled with a reduction rate of 7%. Overall, for the synergistic optimization of microstructure and texture, rolling with a 7% reduction rate followed by annealing at 950 °C in a hydrogen atmosphere is most advantageous.

Numerical modeling investigation of Planar Flow Casting for Fe-6.5wt%Si alloy

Effects of Solidification Cooling Rates on Microstructures and Physical Properties of Fe-6.5%Si Alloys

Effects of Fe-6.5wt.%Si alloys prepared by different cooling methods on ordered structure and mechanical properties

Study on Microstructure and Texture of Fe-3%Si Ultra-Thin Ribbons Prepared by Planar Flow Casting

Effect of wheel speed on the microstructure and magnetic properties of Fe-3.0 wt %Si non-oriented silicon steel ultra-thin ribbons prepared by planar flow casting

Reducing the Core Losses of Fe-Si-B Amorphous Alloy Ribbons by High Cooling Rate Planar Flow Casting

Development of Λ-Fiber Recrystallization Texture and Magnetic Property in Fe–6.5wt% Si Thin Sheet Produced by Strip Casting and Warm Rolling Method

Effects of rolling temperature on microstructure, texture, formability and magnetic properties in strip casting Fe-6.5wt% Si non-oriented electrical steel

Characterization of the Fe-6.5wt%Si Strip with Rapid Cooling Coupling Deep Supercooled Solidification

Optimization of Planar Flow Melt Spinning Process for Producing Thin, Wide, and Continuous Amorphous Ribbons of Fe73.5Si13.5B9Nb3Cu1 Alloys

Fabrication of Fe-6.5wt%Si Ribbons by Melt Spinning Method on Large Scale

The influence of cooling rate on microstructure and magnetic properties of cast Fe-6.5wt%Si steel

Effect of Σ3 grain boundaries on microstructure and properties of oriented Fe-6.5 wt%Si in twin-roll strip casting

Numerical Simulation and Experimental Investigation of Microstructure Evolution and Flow Behavior in the Rheological Squeeze Casting Process of A356 Alloy

Fabrication and properties of strip casting 4.5 wt% Si steel thin sheet

Experimental Study on the Twin Roll Strip Casting and Warm Rolling Fe-6.5 Wt. %si Steel Sheet

Microstructure and texture evolution of thin-gauge non-oriented silicon steel with high permeability produced by twin-roll strip casting

Effect of Cooling Rate on the Microstructure Evolution and Mechanical Properties of Iron-Rich Al–Si Alloy

Effect of Cold Rolling Process on Microstructure, Texture and Properties of Strip Cast Fe-2.6%Si Steel

Solidification structure and crystallographic texture of strip casting 3 wt.% Si non-oriented silicon steel

Twin Roll Casting and Secondary Cooling of 6.0 wt.% Silicon Steel