Annealing temperature effects on microstructure and magnetic properties of Fe-6.5wt. %Si alloy strips prepared by TSTRC process
Dongpo Xuan,Xuming Liu,Ning Xu,Han Guo,Zhiyu Geng,Yitong Wang,Feng Xue
DOI: https://doi.org/10.1016/j.jmmm.2024.172141
IF: 3.097
2024-05-13
Journal of Magnetism and Magnetic Materials
Abstract:The Fe-6.5wt.%Si alloy exhibits remarkable soft magnetic characteristics, such as high magnetic permeability, low coercivity, high resistivity, and nearly zero magnetostriction. These attributes establish it as an ideal material for low-power, low-noise electric motors and transformers. This investigation aimed to assess the impact of annealing temperature (ranging from 800 to 1200 °C for 1 h) on the microstructure, texture, and magnetic properties of a 0.15 mm thick Fe-6.5wt.%Si alloy sheet, which was obtained by subjecting the strips produced through the top side-pouring twin-roll casting (TSTRC) process to multi-pass warm rolling in the temperature range of 600 ∼ 800 °C, avoiding hot rolling. Additionally, the recrystallization mechanism of the annealed sheet at 1100 °C for 1 h was explored. The findings indicate that enhancing the annealing temperature corresponded to a reduction in magnetic induction (B 8 and B 50 ) as well as iron losses (P 10/50 , P 10/400 , and P 2/1000 ). The annealed sheet at 1200 °C for 1 h demonstrated the most favorable magnetic properties, displaying iron losses of 0.486 W/kg, 6.895 W/kg, and 1.232 W/kg for P 10/50 , P 10/400 , and P 2/1000 , respectively. These results illustrate excellent overall magnetic characteristics. The coercivity (Hc) of both B 8 and B 50 decreased as the annealing temperature increased in the hysteresis loop measurements. Specifically, for B 8 , it decreased from 62.84 A/m to 24.50 A/m, and for B 50 , it decreased from 78.10 A/m to 35.50 A/m. The average grain size of the samples gradually increased as the annealing temperature ranged from 800 to 1200 °C. The dominant texture observed was {1 1 1}, and the volume fraction of {1 1 1} texture increased while the volume fractions of {1 0 0} and {1 1 0} textures decreased. Upon annealing at 1100 °C for 8 s, the elongated and flattened deformed structures were mainly replaced by equiaxed grains, indicating the completion of the recrystallization process. However, there was a noticeable distinction in the coarsening degree of equiaxed grains based on their orientations. The presence of λ-oriented grains was less prominent, while α-oriented and γ-oriented grains were relatively more abundant. As the annealing time increased from 8 s to 1 h, there was a decrease in the presence of λ-oriented and α-oriented grains, while the presence of γ-oriented grains significantly increased.
materials science, multidisciplinary,physics, condensed matter