Ultra‐Thin 3.5%Si Steel with Both Magnetic Properties and Mechanical Properties Produced by Different Process Routes of Large‐Scale Production

Yuan Lin,Xiao‐Ge Pei,Hui Wei,Hong‐Xia Wang,Hui‐Hu Lu,Jian‐Xiang Zhao,Xiang Chen,Xiang‐Yu Gu,Shi‐Jia Wang,Li‐Qiang Xue,Wen‐Kang Zhang,Yi‐De Wang

DOI: https://doi.org/10.1002/srin.202400431

IF: 2.1258

2024-09-16

steel research international

Abstract:This article focuses on study of the microstructural and textural evolution, as well as the recrystallization kinetics under different cold‐rolling methods and their influencing mechanism on the properties of the thin‐gauge 3.5%Si nonoriented silicon steel, so as to obtain the best production process, that is, secondary cold rolling with an intermediate annealing temperature of 900 °C. The microstructural and textural evolution, as well as the recrystallization kinetics under different cold‐rolling methods and their influencing mechanism on the properties of the thin‐gauge 3.5%Si nonoriented silicon steel, are investigated by electron backscattering diffraction, X‐ray diffractometer, tensile, and magnetic properties test. The results indicate that compared with the primary cold‐rolling process, the reduction rate of secondary cold‐rolling process is lower (58.3%), and many shear bands are formed in the coarse cold‐rolled sheet, which leads to the formation of strong Goss and cube texture after recrystallization annealing. Owing to the high annealing temperature, the average grain size of finished annealed sheet is little different under different cold‐rolling processes, so the mechanical properties and high‐frequency iron loss are basically the same. The iron loss of the secondary cold‐rolled products decreases with an increase in frequency, and the improvement in the iron loss of the high field (1.5 T) becomes larger than that of the low field (1.0 T). Given the high anisotropy index of the Goss texture, the iron loss anisotropy of the secondary cold‐rolled sheet is higher. Considering the magnetic and mechanical properties, the optimum process is the secondary cold rolling with the intermediate annealing temperature of 900 °C.

metallurgy & metallurgical engineering