Abstract:Dissimilar metal welds (DMWs) between high-Cr martensitic heat-resistant steels and nickel-based alloys with nickel-based filler metals are widely used in fossil-fired power plants. Reports of premature failures of DMW joints have attracted considerable attention as such occurrences in the field can lead to significant economic loss and safety issues. Moreover, a comprehensive understanding of the high-temperature performance of new types of DMWs is lacking. In this work, creep tests were conducted over a stress range of 140-260 MPa at of 600 and 620 'C. A shift in the fracture location with variations in stress was observed, with three typical failure modes. At high stress levels (240-260 MPa), the DMW fractured in the base metal (BM) of martensitic steel, accompanied by a large degree of plastic deformation. At intermediate stress levels (200-240 MPa), the DMW fractured in the fine-grained heat-affected zone (FGHAZ) and the inter-critical heat-affected zone (ICHAZ), with creep cavities around coarsened carbides, indicating a typical type IV crack. At low stress levels (140-200 MPa), the DMW fractured in a mixed mode involving three stages. First, a crack initiated at the interface between the nickel-based weld metal and the martensitic steel, which was attributed to the interaction between the oxidation behavior of the martensitic steels and the thermal stress arising from the mismatch in the coefficients of thermal expansion. Second, the crack deflected into the FGHAZ/ICHAZ and developed into a type IV crack mode. Finally, the crack propagated into the adjacent BM, featuring significant plastic deformation. In addition, in the stress-LMP (Larson-Miller parameter) plot, the creep life at a relatively low stress level was shorter than that predicted by linear extrapolation of the data obtained at a high stress level, indicating a premature failure tendency at low stress. This premature failure tendency can be attributed to microstructure degradation in HAZs and preferential oxidation at the interface at low stress levels.

Cryogenic fracture toughness of high manganese steel joint and 7 %Ni steel joint welded with nickel-based filler metal

Cryogenic Fracture Toughness of 9%ni Steel Flux Cored Arc Welds

The Influence of Microstructure Evolution in Thick Plate 9%ni Steel Submerged Arc Welding Joint on Fracture Toughness Properties

Precipitation behavior of carbides and cryogenic toughness in heat-affected zone of high-Mn twinning-induced plasticity steel welded joint

An extraordinary improvement in cryogenic toughness of K-TIG welded 9Ni steel joint assisted by alternating axial magnetic field

Study on high-cycle fatigue properties of 9 %Ni steel joints welded by GTAW and SAW using nickel-based alloy

Low-cycle Fatigue and Fracture Behaviour of 9%ni Steel Flux Cored Arc Welding Joint at Cryogenic Temperature

Effect of grain size and segregation on the cryogenic toughness mechanism in heat-affected zone of high manganese steel

Tensile Properties and Fracture Behavior of Friction Stir Welded Joints of Fe-32Mn-7Cr-1Mo-0.3N Steel at Cryogenic Temperature

Mechanical properties of cryogenic high manganese steel joints filled with nickel-based materials by SMAW and SAW

Microstructure Characteristics and Properties of Fusion Boundary in 9%ni Steel Joint Filled with Ni-based Alloy

Experimental study of mechanical properties and fracture modes in different regions of the nickel-based welding joint based on small punch test

Investigation of Local Brittle Zone in Multipass Welded Joint of NiCrMoV Steel with Heavy Section

Effect of Gradient Microstructure and Strength Mismatch on Cryogenic Toughness of Fe-Ni Fusion Boundary

Low-cycle Fatigue Behaviors of a New Type of 10% Cr Martensitic Steel and Welded Joint with Ni-based Weld Metal

Dissimilar Laser Welding of CrMnFeCoNi High Entropy Alloy and 316LN Stainless Steel for Cryogenic Application

Microstructure and High Temperature Fracture Toughness of NG-TIG Welded Inconel 617B Superalloy

Design of Novel Fe–Mn–Ni Cryogenic Steel: Microstructure-Property Relationship During Simulated Welding

The Cryogenic Low-Cycle Fatigue Performance of 9%ni Steel Joint Made by Flux Cored Arc Welding

Fracture behavior of C-Mn steel and weld metal in notched and precracked specimens: Part I. fracture behavior

Fracture Location Shift of Dissimilar Metal Welds under Coupled Thermal-Stress Effect