Abstract:Aluminum in terms of electrical conductivity among all known metals ranks fourth after silver, copper and gold. The electrical conductivity of annealed aluminum is approximately 62% IACS of the electrical conductivity of annealed standard copper, which at 20 °C. is taken as 100% IACS. However, due to its low specific gravity, aluminum has a conductivity per unit mass 2 times greater than copper. This property of aluminum gives us an idea of the economic viability of using it as a material for conductors. With equal conductivity (the same length), the aluminum conductor has a cross-sectional area 60% larger than copper, and its mass is only 48% of the mass of copper. In most cases, in electrical engineering, the use of aluminum as a conductor is difficult, and often simply impossible due to its low mechanical strength. An increase in the mechanical strength of aluminum is possible due to the introduction of alloying additives, i.e. creating alloys. In such a case, the mechanical strength increases, causing a noticeable decrease in electrical conductivity. The heat capacity of the aluminum conductor alloy AlTi0.1 (Al + 0.1 wt.% Ti) with calcium in the “cooling” mode was determined from the known heat capacity of the standard aluminum sample. Equations are obtained that describe the cooling rates of specimens made from an aluminum conductor alloy AlTi0.1 with calcium and a reference. Based on the calculated values of the cooling rates of the samples, the equations for the temperature dependence of the heat capacities of the alloys and the standard were formed. The temperature dependences of changes in enthalpy, entropy, and Gibbs energy for the aluminum alloy AlTi0.1 with calcium are calculated by integrating the specific heat capacity. The heat capacity, enthalpy, and entropy of the AlTi0.1 alloy decrease with increasing calcium concentration, and increase with increasing temperature, while the value of the Gibbs energy has an inverse relationship.

The influence of calcium addition on thermophysical properties and thermodynamic functions of aluminum alloy AlCu4.5Mg1

Influence of calcium on specific heat capacity and changes in thermodynamic functions of aluminum conductor alloy AlTi0.1

Heat Capacity and Thermodynamic Functions of the Aluminum Alloy AlCu4.5Mg1 Alloyed with Barium

Temperature Dependences of the Heat Capacity and Thermodynamic Functions of Aluminum Conducting Alloy AlTi0.1 with Strontium

Study of the effect of calcium on structure, physicomechanical and technological properties of deformable alloy Al-3%Mg-0.8%Mn

Quantitative Study of Microstructure-Dependent Thermal Conductivity in Mg-4Ce-xAl-0.5Mn Alloys

Effect of Cooling Rate on Microstructure and Mechanical Properties of Sand-Casted Al–5.0Mg–0.6Mn–0.25Ce Alloy

Influence of small additives of calcium on the structure and properties of ML5 alloy (AZ91)

Effect of Cooling Rate on Microstructure and Mechanical Properties of an Al-5.0Mg-3.0Zn-1.0Cu Cast Alloy

Effect of Al Additions and Cooling Rate on the Microstructure and Mechanical Properties of Austenite FeMnAlC Steels

Effects of heat treatment and testing temperature on the tensile properties of Al–Cu and Al–Cu–Si based alloys

Effect of cooling rate and Al content on solidification characteristics of AZ magnesium alloys using cooling curve thermal analysis

Tailoring Thermal Conductivity and Microstructure of Al-Fe Alloys by Addition of Sc2O3 and Variable Cooling Rates

Molecular Dynamics Studies on the Correlation of Undercoolability and Thermophysical Properties of Liquid Ni–Al Alloys

Thermodynamics of La based La–Al–Cu–Ni–Co alloys studied by temperature modulated DSC

Influence of the Al Content on the Properties of Mechanically Alloyed CoCrFeNiMnXAl20-X High-Entropy Alloys

Hypercooling and the Specific Heat Capacity of Cu-Ni Alloy

Effect of calcium addition on the aluminum alloy A201 foam

Microstructure Evolution and Mechanical Properties of a Cast and Heat-Treated Al–Li–Cu–Mg Alloy: Effect of Cooling Rate During Casting

Influence of Cu/Mg Ratio and Content on Heat-Resistance of Al–Cu–Mg Alloys

Improving the stretch formability of a heat-treatable magnesium–aluminum–calcium–manganese alloy by copper addition at the parts-per-million-level