Effect of Addition of Cu on Microstructure and Some Properties of 5754 Aluminum Alloy

DOI: https://doi.org/10.1007/s12666-023-02904-6

2023-03-18

Transactions of the Indian Institute of Metals

Abstract:In this research paper, the effects of copper addition (0.02 wt.%–7.2 wt.%) on microstructure, mechanical, corrosion, and thermal properties of 5754 aluminum alloy are studied by optical microscope, Brinell hardness testing machine and UTM machine, mass loss test and dilatometer, respectively. Microstructural characterization has shown that increasing copper weight percentage increases grain refinement of the aluminum alloy. The grain size is observed to decrease from 41.7 μm in the case of the 5754 alloys containing 0.02 wt.% Cu to 29.1 μm by the addition of 7.2 wt.% of Cu. XRD studies have revealed that the addition of copper into 5754 aluminum alloy forms precipitates of Al 2 CuMg. The grain refinement and the formation of precipitates increase the Brinell hardness from 41.4 HB in the case of 5754 alloys containing 0.02 wt.% of Cu to 96.8 HB in the case of the alloy containing 7.2 wt.% Cu. However, the intergranular corrosion resistance is observed to decrease with the increase in copper weight percentage. The coefficient of thermal expansion value (between 50 °C to 450 °C) is observed to decrease from 26.9 x 10 -6 (°C) −1 in the case of the 5754 alloys containing 0.02 wt.% of Cu to 25.3 x 10 −6 (°C) −1 in the case of the alloy containing 7.2 wt.% of Cu. The formation of more precipitate phases with the increase in Cu content in the alloy reduces the thermal expansion of the aluminum alloy because of the formation of precipitate phases. The Peak compressive stress value decreases from 1102 MPa (for 5754 alloys) to 502 MPa (sample e) due to forming precipitate phases and reducing solid solutions atoms.

metallurgy & metallurgical engineering