Corrosion inhibition, long-term and adsorption mechanisms of humic acid on ADC12 aluminum alloy in oxalic acid solution

Sudan Liu,Hualiang Huang,Jinbei He
DOI: https://doi.org/10.1007/s10853-024-09981-y
IF: 4.5
2024-07-14
Journal of Materials Science
Abstract:In order to inhibit the corrosion of ADC12 aluminum alloy caused oxalic acid in engine coolant, corrosion inhibitor technology is usually used because of its simple operation, low cost, no impact on metal heat dissipation, and effectively suppressing metal corrosion at a lower concentration. In this paper, the corrosion inhibition, long-term and adsorption mechanisms of humic acid (HA) on ADC12 aluminum alloy were studied using electrochemical testing, surface analysis techniques, and theoretical calculations. The results showed that HA was a mixed corrosion inhibitor that followed the Langmuir adsorption model and belonged to physical chemical mixed adsorption. The corrosion inhibition efficiency of HA was the highest at a concentration of 1500 ppm and enhanced with the extension of soaking time. After soaking for 72 h, the corrosion inhibition efficiency of HA reached its maximum (92.7%), indicating that HA had a good long-term corrosion inhibition effect. HA had a high adsorption energy on the surface of ADC12 aluminum alloy, and HA molecules adsorbed on its surface through the carboxyl groups linked to N atom to form a protective corrosion inhibitor film, effectively inhibiting its corrosion.
materials science, multidisciplinary
What problem does this paper attempt to address?