Inhibition by tetradecylpyridinium bromide of the corrosion of aluminium in hydrochloric acid solution
Xianghong Li,Shuduan Deng,Hui Fu
DOI: https://doi.org/10.1016/j.corsci.2011.01.032
IF: 7.72
2011-01-01
Corrosion Science
Abstract:Research highlights ► Tetradecylpyridinium bromide (TDPB) is found to be a good inhibitor for the corrosion of alunimium in 1.0 M HCl. ► The adsorption of TDPB on aluminium surface obeys Langmuir adsorption isotherm. ► TDPB acts as a cathodic-type inhibitor. ► EIS diagram appears an elliptic shape. The presence of TDPB in 1.0 M HCl solutions enhances R t values while reduces C dl values. Abstract The inhibition effect of tetradecylpyridinium bromide (TDPB) on the corrosion of aluminium in 1.0 M HCl solution was studied by weight loss, potentiodynamic polarization, and electrochemical impedance spectroscopy (EIS) methods. The results show that TDPB is a very good inhibitor at little concentrations, and the adsorption of TDPB on aluminium surface obeys Langmuir adsorption isotherm. Polarization curves reveal that TDPB behaves as a cathodic inhibitor. EIS spectra consist of large capacitive loop at high frequencies followed by a large inductive one at low frequency values, and confirm the inhibitive ability. Keywords A. Aluminium B. EIS B. Polarization B. Weight loss C. Acid inhibition 1 Introduction Hydrochloric acid is often used as industrial acid cleaning, chemical or electrochemical etching, and acid pickling of Al. It shows strong corrosiveness on aluminium, so it is necessary to seek inhibitors for the corrosion of aluminium in HCl. An extensive review of the literature has shown that the main attention is paid to inhibition studies on aluminium in HCl using organic inhibitors. Up to now, various organic compounds are reported as good corrosion inhibitors for aluminium in hydrochloric acid media, such as aliphatic amines [1,2] , aromatic amines [3] , aromatic aldehyde [4] , carbonyl compounds [5] , phenol [6] , thiosemicarbazide derivatives [7] , hydrazine derivatives [8,9] , pyridine derivatives [10] , tetrazole derivatives [11] , amino acids [12] , antibacterial drugs [13,14] , Schiff bases [15–17] , alkylimidazolium ionic liquids [18] and organic dye [19] . It has been assumed that the organic compound exert its inhibition by adsorption on the metal surface. Besides the above mentioned organic inhibitors, the surfactant inhibitor has many advantages such as high inhibition efficiency, low price, low toxicity and easy production [20] . The adsorption of surfactant on metal surface can markedly change the corrosion-resisting property of the metal [21] , and so the study of the relationship between adsorption and corrosion inhibition is of great importance. In previous investigations, some anionic surfactants [22–24] and nonionic surfactants [25,26] have been used for the corrosion inhibition of aluminium in hydrochloric acid media. Although the studied anionic surfactants show good inhibitive performance, they are poor bactericides, and easily destroyed by strong electrolyte, and produces the salting-out effect. On the other hand, as another typical kind of surfactants, the cationic surfactants are cost effective, and stable in acid and base solutions, and good bactericide. It is found that cationic surfactants [21,27–31] have shown high inhibition efficiency for steel corrosion in acid solutions. However, little work appears to have been done on the inhibition of aluminium corrosion in acid solution by cationic surfactants. In 2001, Abd El Rehim et al. [32] studied the inhibition action of a cationic surfactant of 1,1(lauryl amido)propyl ammonium chloride on the corrosion of aluminium in 1.0 M HCl. Surfactants exert the inhibition action by adsorption on the metal surfaces such that chemical structure of the ionic head (hydrophilic part) attacks the metal surface while its tail (hydrophobic part) extends to the solution face. The influence of the chemical structure of ionic head on inhibition efficiency was studied by Saleh and Atia [30] , and the results showed that the heterocyclic systems bearing a quarternized nitrogen atom give better inhibition performance than the alkyl substituted quaternary ammonium compounds. On the other hand, the hydrophobic carbon chain length also plays an important role in the inhibition efficiency, and the augmentations of the hydrophobic hydrocarbon chain length often raise the protection effect. But the rather long hydrocarbon chain length can also lead to poor water solubility and corresponding low inhibition efficiency. Accordingly, the hydrocarbon chain length should be suitable. By considering the cumulative effect of hydrocarbon chain length and ionic head, tetradecylpyridinium bromide (TDPB) is employed for the corrosion inhibitor. Namely, the hydrocarbon chain length of TDPB (C 14 H 29 –) is suitable, and the ionic head is –N + with a pyridinium ring. Moreover, TDPB has good solubility in water, easy production with low cost, and nontoxic. However, to our best of knowledge, it has not yet been investigated as an inhibitor for aluminium in hydrochloric acid. In the present work, the inhibition effect of TDPB on the corrosion of aluminium in 1.0 M HCl solution was investigated by weight loss, potentiodynamic polarization and electrochemical impedance spectroscopy (EIS) methods. Meanwhile, thermodynamic parameters including adsorption enthalpy Δ H 0 , adsorption free energy Δ G 0 and adsorption entropy Δ S 0 were calculated and discussed. It is expected to get useful information on the inhibition effect of TDPB on aluminium corrosion in hydrochloric acid solution. 2 Experimental 2.1 Materials Tests were performed on aluminium of the following composition (wt.%): Si 0.25%, Fe 0.35%, Cu 0.05%, Mn 0.03%, Mg, 0.03%, Zn, 0.05%, Ti 0.03%, V 0.05%, and the remainder Al. 2.2 Inhibitor Tetradecylpyridinium bromide (TDPB) was obtained from Shanghai Chemical Reagent Company of China. Fig. 1 shows the molecular structure of TDTB. 2.3 Solutions The aggressive solution of 1.0 M HCl was prepared by dilution of AR grade 37% HCl. The concentration range of TDPB employed was 0.05–1.0 mM. 2.4 Weight loss measurements The aluminium sheets of 2.5 cm × 2.0 cm × 0.20 cm were abraded by a series of emery paper (grade 320–500–800) and then washed with distilled water, degreased with acetone, and finally dried with a cold air stream. After weighing accurately by digital balance with a sensitivity of ±0.1 mg, the specimens were immersed in a beaker containing 250 ml hydrochloric acid solution without and with different concentrations of TDPB using glass hooks and rods. The temperature was controlled at 20 °C by a water thermostat. All the aggressive acid solutions were open to air. After immersion for 6 h, the specimens were taken out, washed with bristle brush under running water in order to remove the corrosion product, dried with a hot air stream, and reweighed accurately. In order to get good reproducibility, experiments were carried out in duplicate. The average weight loss of two parallel aluminium sheets was obtained. Then the experiments were repeated at different temperature. The corrosion rate ( v ) is calculated by the following equation [22] : (1) v = W St where W is the average weight loss of two parallel aluminium sheets, S the total area of one aluminium specimen, and t is immersion time (6 h). With the calculated corrosion rate, the inhibition efficiency ( E w ) is calculated as follows [33] : (2) E w % = v 0 - v v 0 × 100 where v 0 and v are the values of corrosion rate without and with inhibitor, respectively. 2.5 Electrochemical measurements Electrochemical experiments were carried out in a conventional three-electrode cell with a platinum counter electrode (CE) and a saturated calomel electrode (SCE) coupled to a fine Luggin capillary as the reference electrode. In order to minimize ohmic contribution, the Luggin capillary was kept close to the working electrode (WE) which was in the form of a square aluminium embedded in a PVC holder using epoxy resin so that the flat surface was only surface in the electrode. The WE surface area was 1.0 cm × 1.0 cm, abraded with emery paper (grade 320–500–800) on test face, rinsed with distilled water, degreased with acetone, and dried with a cold air stream. Before measurement the electrode was immersed in test solution at open circuit potential (OCP) for 1 h at 20 °C to attain a stable state. All electrochemical measurements were carried out using a PARSTAT 2273 advanced electrochemical system (Princeton Applied Research). The potential of potentiodynamic polarization curves was done from a potential of −250 mV vs. OCP, to 250 mV vs. OCP at a sweep rate of 0.5 mV s −1 . Inhibition efficiency ( E p %) is defined as: (3) E p % = I corr - I corr(inh) I corr × 100 where I corr and I corr(inh) represent corrosion current density values without and with inhibitor, respectively. Electrochemical impedance spectroscopy (EIS) was carried out at OCP in the frequency range of 10 mHz–100 kHz using a 10 mV peak-to-peak voltage excitation. Inhibition efficiency ( E R %) is calculated on the basis of the equation: (4) E R % = R t(inh) - R t(0) R t(inh) × 100 where R t(0) and R t(inh) are charge transfer resistance values in the absence and presence of inhibitor, respectively. 3 Results and discussion 3.1 Weight loss measurements 3.1.1 Effect of TDPB on corrosion rate Fig. 2 shows the corrosion rate values of aluminium in the presence of different concentrations of TDPB in 1.0 M HCl at various temperatures. The corrosion rate values (g m −2 h −1 ) decrease as TDPB concentration increases, i.e., corrosion inhibition enhances with the inhibitor concentration. This behaviour is due to the fact the adsorption amount and the coverage of inhibitor on aluminium surface increase with the inhibitor concentration [22] . It should be noted that when the inhibitor concentration reaches approximately 0.5 mM at 20 and 25 °C, the corrosion rate values reach certain values and do not change remarkably. In this situation, it is likely for the surfactant to form micelle near concentration range, and the corrosion inhibition reaches a steady state. At 30–40 °C, that steady state shifts to 1 mM. Fig. 2 also presents that the corrosion rate increases with the temperature both in uninhibited and inhibited solutions. But the corrosion rate increases more rapidly with temperature in the absence of inhibitor. These results confirm that TDPB acts as an efficient inhibitor in the range of temperature studied. 3.1.2 Effect of TDPB on inhibition efficiency The values of inhibition efficiency obtained from weight loss ( E w ) for different inhibitor concentrations in 1.0 M HCl at 20–40 °C is shown in Fig. 3 . At all temperatures studied, E w increases as the concentration of inhibitor increases from 0.05 to 1.0 mM. At 1.0 mM, the maximum E w at 20 °C is 95.6%; at 25 °C, 94.9%; at 30 °C, 93.7%; at 35 °C, 90.3%; and at 40 °C, 87.2%. So TDPB is a good inhibitor for aluminium in 1.0 M HCl. Under similar conditions (1.0 M HCl), the inhibition efficiency for anionic surfactant of sodium dodecyl benzene sulphonate (SDBS) is 60.72% at 2.0 mM [23] ; and for nonionic surfactant of OL(EO) 80 , 66.7% at 1.0 mM [25] . Therefore, TDPB shows better inhibition performance comparing with SDBS and OL(EO) 80 . Fig. 3 also shows that E w decreases with increase in temperature from 20 to 40 °C. The reason can be attributed to that the higher temperatures might cause the desorption of TDPB from aluminium surface and the corrosion is also increased by the temperature effect on its velocity. 3.1.3 Adsorption isotherm Basic information on the interaction between inhibitor and aluminium surface can be provided by adsorption isotherm. Attempts were made to fit to various isotherms including Frumkin, Langmuir, Temkin, Freundlich, Bockris–Swinkels and Flory–Huggins isotherms. By far the results were best fitted by Langmuir adsorption isotherm equation [34] : (5) c θ = 1 K + c where c is the concentration of inhibitor, K the adsorptive equilibrium constant and θ is the surface coverage and calculated by the following equation [34] : (6) θ = v 0 - v v 0 The linear regressions parameters between c / θ and c are listed in Table 1 . Straight lines of c / θ vs. c at different temperatures are shown in Fig. 4 . It is observed that all linear correlation coefficients ( r ) are almost equal to 1 and all slopes are close to 1, which indicates the adsorption of TDPB on aluminium surface obeys Langmuir adsorption isotherm. The adsorptive equilibrium constant ( K ) value decreases with increasing temperature, which could be attributed to the desorption of inhibitor molecules at higher temperature. In addition, large values of K mean better inhibition efficiency of a given inhibitor. This is in good agreement with the values of E w obtained from Fig. 3 . 3.1.4 Thermodynamic parameters Thermodynamic parameters play an important role in understanding the inhibitive mechanism. The standard adsorption heat (Δ H 0 ) could be calculated according to Van’t Hoff equation [22] : (7) ln K = - Δ H 0 RT + constant where R is the gas constant (8.314 J K −1 mol −1 ), T the absolute temperature (K). Fig. 5 shows the straight line of ln K vs. 1/ T , and the linear correlation coefficient ( r ) is 0.9980. The standard adsorption free energy (Δ G 0 ) is obtained according to [35] : (8) K = 1 55.5 exp - Δ G 0 RT where the value 55.5 is the concentration of water in solution expressed in M. Then the standard adsorption entropy (Δ S 0 ) can be obtained by the following basic thermodynamic equation: (9) Δ S 0 = Δ H 0 - Δ G 0 T All the calculated thermodynamic parameters are listed in Table 2 . The negative sign of Δ H 0 shows that the adsorption of TDPB is an exothermic process [33] , which confirms that inhibition performance decreases with temperature. Such behaviour can be interpreted on the basis that increasing temperature resulted in desorption of some adsorbed inhibitor molecules from the metal surface. The negative values of Δ G 0 indicate that the adsorption of inhibitor molecule onto aluminium surface is spontaneous. Generally, values of Δ G 0 up to −20 kJ mol −1 are consistent with the electrostatic interaction between the charged molecules and the charged metal (physical adsorption) while those more negative than −40 kJ mol −1 involve sharing or transfer of electrons from the inhibitor molecules to the metal surface to form a co-ordinate type of bond (chemisorption) [36] . In the present study, the value of Δ G 0 is within the range from −40 to −20 kJ mol −1 ; probably means that both physical adsorption and chemical adsorption would take place. The negative values of Δ S 0 mean that the process of adsorption is accompanied by a decrease in entropy. It might be explained as follows: before the adsorption of surfactant onto the aluminium surface, the chaotic degree of corroded aluminium surface is high, but when inhibitor molecules are orderly adsorbed onto the aluminium surface, as a result, a decrease in entropy. Values of Δ H 0 and Δ S 0 can be also calculated by the thermodynamic fundamental equation Δ G 0 = Δ H 0 − T Δ S 0 . Fig. 6 clearly shows that the good dependence of Δ G 0 on T (linear regression coefficient r = 0.9872), indicating the good correlation among thermodynamic parameters. From the slope and intercept of the straight line of Δ G 0 vs. T , the calculated values ofΔ H 0 andΔ S 0 are −105.4 kJ mol −1 and −232.1 J mol −1 K −1 , respectively, which are very close to those obtained in Table 2 . So values ofΔ H 0 andΔ S 0 obtained by the both method are in good agreement. 3.2 Polarization curves Potentiodynamic polarization curves for aluminium in 1.0 M HCl containing various concentrations of TDPB at 20 °C are shown in Fig. 7 . The presence of inhibitor causes a prominent decrease in the corrosion rate, i.e., shifts the cathodic curves to lower values of current densities to more extent. On the other hand, the anodic reaction of the corrosion process is slightly inhibited. This means that the used surfactant mainly acts as a cathodic inhibitor. As is evident from Fig. 7 , the cathodic polarization curves indicate that the hydrogen evolution reaction is activation controlled since the cathodic portions rise to Tafel lines, and the presence of the TDPB does not affect the mechanism of hydrogen reaction, owing to the parallel cathodic polarization curves. It is important to note that in anodic domain, it is impossible to recognize the linear Tafel regions. Accordingly, the corrosion current density values are estimated accurately by extrapolating the cathodic linear region back to the corrosion potential. Similar fitting method has been used for aluminium in HCl [16] and H 3 PO 4 [37] solutions in the presence of organic inhibitors. The electrochemical corrosion parameters of corrosion current densities ( I corr ), corrosion potential ( E corr ), cathodic Tafel slope ( b c ), and the inhibition efficiency ( E p ) as functions of TDPB concentration, are given in Table 3 . It is apparent that I corr decreases considerably in the presence of TDPB, and decreases with increasing the inhibitor concentration. Correspondingly, E p increases with the inhibitor concentration, due to the increase in the blocked fraction of the electrode surface by adsorption. E p of 1.0 mM inhibitor reaches up to a maximum of 97.4%, which indicates that TDPB is a good inhibitor for aluminium in 1.0 M hydrochloric acid. The presence of TDPB shifts E corr to negative, which indicates that TDPB acts as a cathodic-type inhibitor [38] . Tafel slope of b c changes significantly upon addition of TDPB, which means that the TDPB molecules are more adsorbed on the cathodic sites resulting in an inhibition of the cathodic reduction reactions. From Table 3 it can be concluded that values of E w and E p are in good agreement. 3.3 Electrochemical impedance spectroscopy (EIS) Fig. 8 represents the Nyquist diagrams for aluminium in 1.0 M HCl at 20 °C without and with various concentrations of TDPB. The impedance spectra consist of a large capacitive loop at high frequencies followed by a large inductive one at low frequency values. Generally, the low frequency inductive loop is always observed for aluminium in hydrochloric acid [11,16,18] , and the diameter of inductive loop is usually smaller than that of higher frequency capacitive loop. However, in the present system, the size of capacitive loop is almost equal to that of inductive loop. In other words, the whole diagram appears an elliptic shape. Similar shape is also found for aluminium in acid solution inhibited by 8-hydroxy-quinoline [39] and Al–Cu alloy in hydrochloric acid [40] . After adding TDPB, the shape is not changed throughout all tested concentrations, indicating that almost no change in the corrosion mechanism occurs due to the inhibitor addition [41] . According to Bessone et al. [42] and Brett [43] , the high frequency capacitive loop could be attributed to the oxide layer on Al. In the experiments, it is reasonable to assume that the electrode surface has been covered with an oxide layer because of the ex situ pretreatment of the electrode. In fact, it is very difficult to produce an oxide free Al surface. Even after producing such a surface, it is repassivated very fast by oxygen [44] . It can be correlated with dielectric properties of a surface layer; i.e. [metal-oxide–hydroxide-inhibitor] ads complex [45] . On the other hand, the origin of the large inductive loop at low frequency is still unclear. Adsorbed charged intermediates may result in an inductive loop [37] . This is more pronounced when the intermediates are strongly adsorbed. Lenderink et al. [46] have attributed to the relaxation of adsorbed species like H ads + . Other suggested relaxation adsorbed intermediates include Cl − [40] , oxygen ion [47] or inhibitor species [48] on the electrode surface. It might be also attributed to the re-dissolution of the oxide layer surface [32] or Al-dissolution [40] at low frequencies. Inductive behaviour is also observed for the pitted active state and attributed to the surface area modulation or salt film property modulation [49] . Nevertheless, the sizes of both capacitive and inductive loops increase significantly with the inhibitor concentration. This indicates that the impedance of inhibited substrate increases with TDPB concentration. Owing to the unique Nyquist diagrams, it is difficult to find suitable equivalent circuit to fit the EIS results. The high frequency capacitive loop is usually related to the charge transfer of the corrosion process and double layer behaviour. Thus, in the present system, only two important electrochemical parameters of charge transfer resistance ( R t ) and double layer capacitance ( C dl ) are calculated from the large capacitive loop. Noticeably, these high frequency loops are not perfect semicircles which can be attributed to the frequency dispersion as a result of the roughness and inhomogeneous of electrode surface [50] . The EIS results of high frequency capacitive loops are simulated by the equivalent circuit shown in Fig. 9 to pure electric models that could verify or rule out mechanistic models and enable the calculation of numerical values corresponding to the physical and/or chemical properties of the electrochemical system under investigation [51] . The circuit employed allows the identification of both solution resistance ( R s ) and charge transfer resistance ( R t ). It is worth mentioning that the double layer capacitance ( C dl ) value is affected by imperfections of the surface, and that this effect is simulated via a constant phase element (CPE) [52] . The CPE is composed of a component Q dl and a coefficient a , and a quantifies different physical phenomena like surface inhomogeneousness resulting from surface roughness, inhibitor adsorption, porous layer formation, etc. So the capacitance is deduced from the following relation [53] : (10) C dl = Q dl × ( 2 π f max ) a - 1 where f max represents the frequency at which imaginary value reaches a maximum on the Nyquist plot. The electrochemical parameters of R t , C dl and E R are calculated by ZSimpWin software and presented in Table 4 . Inspection of Table 4 reveals that R t values increases prominently while C dl reduces with the concentration of TDPB. The decrease in C dl comparing with that in blank solution (without inhibitor), which can result from a decrease in local dielectric constant and/or an increase in the thickness of the electrical double layer, suggests that the inhibitor molecules function by adsorption at the metal/solution interface [54,55] . E R increases with the concentration of TDPB, and the maximum E R reaches up to 97.4%, which further confirm TDPB exhibits very good inhibitive performance for aluminium in 1.0 M H 2 SO 4 . Inhibition efficiencies obtained from weight loss ( E w ), potentiodynamic polarization curves ( E p ) and EIS ( E R ) are in good reasonably agreement. 3.4 Explanation for inhibition The inhibition mechanism can be proposed from the adsorption of inhibitor on metal surface. TDPB is ionized in the acid solution as following: (11) TDPB → [ TDP ] + + Br - Thus, in aqueous acidic solutions, the TDPB exists as the cation organic part ([TDP] + ) and the anion inorganic part (Br − ) in aqueous acidic solutions. Accordingly, TDPB exerts inhibition action by adsorption of [TDP] + on aluminium surface through that hydrophilic part pyridine ring (the polar or ionic group) attacks the metal surface while the hydrophobic part C 14 H 29 – extends to solution face to form a hydrophobic barrier to decrease the corrosion rate. In view of the long hydrocarbon chain length of TDPB (C 14 H 29 –), it is difficult for TDPB adsorb on the aluminium surface with perpendicular orientation of pyridinium ring. On the other hand, the planar adsorption of pyridinium ring with tilted orientation of alkyl chain (C 14 H 29 –) extending to solution should be more reasonable. This mode of adsorption is shown in Fig. 10 . Four types of adsorption may take place in the inhibiting phenomena involving organic molecules on aluminium surface as follows: (i) The value of pH zch , which is defined as the threshold pH at a point of zero charge, is equal to 9.1 for aluminium [56] . In the present system (1.0 M HCl solution), pH is 0. So the aluminium surface charges positive charge in 1.0 M HCl solution. Since the anions of Cl − could be specifically adsorbed, and the anodic dissolution of Al in hydrochloric acid follows the steps [16] : (12) Al + Cl - ⇌ AlCl ads - (13) AlCl ads - + Cl - → AlCl 2 + + 3 e - Through electrostatical attraction, the positive [TDP] + could adsorb on the negatively charged AlCl ads - species as shown in Fig. 10 a. Thus the following reaction of AlCl ads - to AlCl 2 + as shown by above reaction (12) can be prevented. (ii) Besides to the physical adsorption, [TDP] + may be adsorbed on the metal surface via the chemisorption mechanism, involving to the coordinate bonds that may be formed between the lone electrons pairs of N atom and the empty p-orbitals of Al atoms which enhanced the combination intension between the inhibitor molecule and electrode surface ( Fig. 10 b). (iii) [TDP] + has plentiful π-electrons owing to aromatic rings, they can be also adsorbed on the metal surface on the basis of donor–acceptor interactions between π-electrons of the pyridine ring and vacant p-orbitals of Al ( Fig. 10 c). (iv) A combination of the above. 4 Conclusion (1) TDPB acts as a good inhibitor for the corrosion of aluminium in 1.0 M HCl. Inhibition efficiency increases with the inhibitor concentration, while decreases with the temperature. (2) The adsorption of TDPB on aluminium surface obeys Langmuir adsorption isotherm. The adsorption process is spontaneous and exothermic accompanied by a decrease in entropy. (3) TDPB acts as a cathodic-type inhibitor. EIS spectra exhibit a large capacitive loop at high frequencies followed by a large inductive one at low frequency values. The presence of TDPB in 1.0 M HCl solutions enhances R t values while reduces C dl values. (4) The adsorption of TDPB involves electrostatic attraction between AlCl ads - and [TDP] + , sharing electrons between the N atoms and vacant p-orbitals of Al, donor–acceptor interactions between π-electrons of pyridine ring and vacant p-orbitals of Al. Acknowledgement This work was carried out in the frame of research project funded by Key Construction Course of Chemical Engineering for Forest Products of Southwest Forestry University (XKX200907), and Applied Fundamental Research Foundation of Yunnan Province (2009CD072). The electrochemical measurements were carried out on PARSTAT 2273 advanced electrochemical system (Princeton Applied Research) provided by Advanced Science Instrument Sharing Center of Southwest Forestry University. References [1] M.N. Desai B.C. Thakar P.M. Chhaya M.H. Gandhi Inhibition of corrosion of aluminium-51S in hydrochloric acid solutions Corros. Sci. 16 1976 9 24 [2] H.A. El-Dahan T.Y. Soror R.M. El-Sherif Studies on the inhibition of aluminum dissolution by hexamine–halide blends: Part I. Weight loss, open circuit potential and polarization measurements Mater. Chem. Phys. 89 2005 260 267 [3] I.B. Obot N.O. Obi-Egbedi S.A. Umoren The synergistic inhibitive effect and some quantum chemical parameters of 2,3-diaminonaphthalene and iodide ions on the hydrochloric acid corrosion of aluminium Corros. Sci. 51 2009 276 282 [4] A.Y. El-Etre Inhibition of acid corrosion of aluminum using vanillin Corros. Sci. 43 2001 1031 1039 [5] I.M. Issa M.N.H. Moussa M.A.A. Ghandour A study on the effect of some carbonyl compounds on the corrosion of aluminium in hydrochloric acid solution Corros. Sci. 10 1973 791 797 [6] M. Lashgari A.M. Malek Fundamental studies of aluminum corrosion in acidic and basic environments: theoretical predictions and experimental observations Electrochim. Acta 55 2010 5253 5257 [7] A.S. Fouda M.N. Moussa F.I. Taha A.I. Elneanaa The role of some thiosemicarbazide derivatives in the corrosion inhibition of aluminium in hydrochloric acid Corros. Sci. 26 1986 719 726 [8] M.N.H. Moussa F.I.M. Taha M.M.A. Gouda G.M. Singab The effect of some hydrazine derivatives on the corrosion of Al in HCl solution Corros. Sci. 16 1976 379 385 [9] S.M. Hassan Y.A. Elawady A.I. Ahmed A.O. Baghlaf Studies on the inhibition of aluminium dissolution by some hydrazine derivatives Corros. Sci. 19 1979 951 959 [10] Y. Xiao-Ci Z. Hong L. Ming-Dao R. Hong-Xuan Y. Lu-An Quantum chemical study of the inhibition properties of pyridine and its derivatives at an aluminum surface Corros. Sci. 42 2000 645 653 [11] K.F. Khaled M.M. Al-Qahtani The inhibitive effect of some tetrazole derivatives towards Al corrosion in acid solutions: chemical electrochemical and theoretical studies Mater. Chem. Phys. 113 2009 150 158 [12] G. Bereket A. Yurt The inhibition effect of amino acids and hydroxy carboxylic acids on pitting corrosion of aluminum alloy 7075 Corros. Sci. 43 2001 1179 1195 [13] M. Abdallah Antibacterial drugs as corrosion inhibitors for corrosion of aluminium in hydrochloric solution Corros. Sci. 46 2004 1981 1996 [14] I.B. Obot N.O. Obi-Egbedi S.A. Umoren Antifungal drugs as corrosion inhibitors for aluminium in 0.1 M HCl Corros. Sci. 51 2009 1868 1875 [15] G.K. Gomma M.H. Wahdan Schiff bases as corrosion inhibitors for aluminium in hydrochloric acid Mater. Chem. Phys. 39 1995 209 213 [16] A. Yurt S. Ulutas H. Dal Electrochemical and theoretical investigation on the corrosion of aluminium in acidic solution containing some Schiff bases Appl. Surf. Sci. 253 2006 919 925 [17] H. Ashassi-Sorkhabi B. Shabani B. Aligholipour D. Seifzadeh The effect of some Schiff bases on the corrosion of aluminum in hydrochloric acid solution Appl. Surf. Sci. 252 2006 4039 4047 [18] Q.B. Zhang Y.X. Hua Corrosion inhibition of aluminum in hydrochloric acid solution by alkylimidazolium ionic liquids Mater. Chem. Phys. 119 2010 57 64 [19] E.E. Oguzie B.N. Okolue E.E. Ebenso G.N. Onuoha A.I. Onuchukwu Evaluation of the inhibitory effect of methylene blue dye on the corrosion of aluminium in hydrochloric acid Mater. Chem. Phys. 87 2004 394 401 [20] D.N. Singh A.K. Dey Synergistic effects of inorganic and organic cations on inhibitive performance of propargyl alcohol on steel dissolution in boiling hydrochloric acid solution Corrosion 49 1993 594 600 [21] M. Elachouri M.S. Hajji M. Salem S. Kertit R. Coudert E.M. Essassi Some surfactants in the series of 2-(alkyldimethylammonio) alkanol bromides as inhibitors of the corrosion of iron in acid chloride solution Corros. Sci. 37 1995 381 389 [22] T.P. Zhao G.N. Mu The adsorption and corrosion inhibition of anion surfactants on aluminium surface in hydrochloric acid Corros. Sci. 41 1999 1937 1944 [23] S.S. Abd El Rehim H.H. Hassaan M.A. Amin The corrosion inhibition study of sodium dodecylbenzene sulphonate to aluminium and its alloys in 1.0 M HCl solution Mater. Chem. Phys. 78 2002 337 348 [24] A.K. Maayta N.A.F. Al-Rawashdeh Inhibition of acidic corrosion of pure aluminum by some organic compounds Corros. Sci. 46 2004 1129 1140 [25] E.E. Foad El-Sherbini S.M. Abd-El-Wahab M.A. Deyab Studies on corrosion inhibition of aluminum in 1.0 M HCl and 1.0 M H 2 SO 4 solutions by ethoxylated fatty acids Mater. Chem. Phys. 82 2003 631 637 [26] V. Branzoi F. Golgovici F. Branzoi Aluminium corrosion in hydrochloric acid solutions and effect of some organic inhibitors Mater. Chem. Phys. 78 2002 122 131 [27] D.P. Schweinsberg V. Ashworth The inhibition of the corrosion of pure iron in 0.5 M sulphuric acid by n -alkyl quaternary ammonium iodides Corros. Sci. 28 1988 539 545 [28] L. Niu H. Zhang F. Wei S. Wu X. Cao P. Liu Corrosion inhibition of iron in acidic solutions by alkyl quaternary ammonium halides: correlation between inhibition efficiency and molecular structure Appl. Surf. Sci. 252 2005 1634 1642 [29] T. Vasudevan S. Muralidharan S. Alwarappan S.V.K. Iyer The influence of N -hexadecyl benzyl dimethyl ammonium chloride on the corrosion of mild steel in acids Corros. Sci. 37 1995 1235 1244 [30] M.M. Saleh A.A. Atia Effects of structure of the ionic head of cationic surfactant on its inhibition of acid corrosion of mild steel J. Appl. Electrochem. 36 2006 899 905 [31] A.A. Atia M.M. Saleh Inhibition of acid corrosion of steel in cetylpyridinium chloride J. Appl. Electrochem. 33 2003 171 177 [32] S.S. Abd El Rehim H.H. Hassan M.A. Amin Corrosion inhibition of aluminum by 1,1(lauryl amido)propyl ammonium chloride in HCl solution Mater. Chem. Phys. 70 2001 64 72 [33] X.H. Li S.D. Deng H. Fu T.H. Li Adsorption and inhibition of 6-benzylaminopurine on cold rolled steel in 1.0 M HCl Electrochim. Acta 54 2009 4089 4098 [34] X.H. Li S.D. Deng H. Fu Synergism between red tetrazolium and uracil on the corrosion of cold rolled steel in H 2 SO 4 solution Corros. Sci. 51 2009 1344 1355 [35] E. Cano J.L. Polo A. La Iglesia J.M. Bastidas A study on the adsorption of benzotriazole on copper in hydrochloric acid using the inflection point of the isotherm Adsorption 10 2004 219 225 [36] F. Bentiss M. Lebrini M. Lagrenée Thermodynamic characterization of metal dissolution and inhibitor adsorption processes in mild steel/2, 5-bis( n -thienyl)-1,3,4-thiadiazoles/hydrochloric acid system Corros. Sci. 47 2005 2915 2931 [37] M.A. Amin Q. Mohsen O.A. Hazzai Synergistic effect of I − ions on the corrosion inhibition of Al in 1.0 M phosphoric acid solutions by purine Mater. Chem. Phys. 114 2009 908 914 [38] C.N. Cao, Corrosion Electrochemistry Mechanism, Chemical Industrial Engineering Press, Beijing, 2004, p. 235 (in Chinese). [39] L. Garrigues N. Pebere F. Dabosi An investigation of the corrosion inhibition of pure aluminum in neutral and acidic chloride solutions Corros. Sci. 41 1996 1209 1215 [40] E.A. Noor Evaluation of inhibitive action of some quaternary N-heterocyclic compounds on the corrosion of Al–Cu alloy in hydrochloric acid Mater. Chem. Phys. 114 2009 533 541 [41] N. Labjar M. Lebrini F. Bentiss N.E. Chihib S. El Hajjaji C. Jama Corrosion inhibition of carbon steel and antibacterial properties of aminotris-(methylnephosnic) acid Mater. Chem. Phys. 119 2010 330 336 [42] J. Bessone C. Mayer K. Jutter W. Lorenz AC-impedance measurements on aluminium barrier type oxide films Electrochim. Acta 28 1983 171 175 [43] C.M.A. Brett On the electrochemical behaviour of aluminium in acidic chloride solution Corros. Sci. 33 1992 203 210 [44] G.T. Burstein R.J. Cinderey The potential of freshly generated metal surfaces determined from the guillotined electrode—a new technique Corros. Sci. 32 1992 1195 1211 [45] M. Metlkoš-Huković R. Babić Z. Grubac Corrosion protection in acidic chloride solutions with nontoxic inhibitors J. Appl. Electrochem. 28 1998 433 439 [46] H.J.W. Lenderink M.V.D. Linden J.H.W. De Wit Corrosion of aluminium in acidic and neutral solutions Electrochim. Acta 38 1993 1989 1992 [47] T. Valand K.E. Heusler Reactions at the oxide-electrolyte interface of anodic oxide films on aluminum J. Electroanal. Chem. 149 1983 71 82 [48] A.K. Singh M.A. Quraishi Effect of cafazolin on the corrosion of mild steel in HCl solution Corros. Sci. 52 2010 152 160 [49] J.B. Bessone D.R. Salinas C. Mayer M. Ebert W.J. Lorenz An EIS study of aluminium barrier-type oxide films formed in different media Electrochim. Acta 37 1992 2283 2290 [50] M. Lebrini M. Lagrenée H. Vezin M. Traisnel F. Bentiss Experimental and theoretical study for corrosion inhibition of mild steel in normal hydrochloric acid solution by some new macrocyclic polyether compounds Corros. Sci. 49 2007 2254 2269 [51] A.R.S. Priya V.S. Muralidharam A. Subramania Development of novel acidizing inhibitors for carbon steel corrosion in 15% boiling hydrochloric acid Corrosion 64 2008 541 552 [52] P. Bommersbach C. Alemany-Dumont J.P. Millet B. Normand Hydrodynamic effect on the behaviour of a corrosion inhibitor film: characterization by electrochemical impedance spectroscopy Electrochim. Acta 51 2006 4011 4018 [53] Q. Qu Z.Z. Hao L. Li W. Bai Y.J. Liu Z.T. Ding Synthesis and evaluation of Tri-hydroxymethyl-(2-hydroxybenzylidenamino)-methane as a corrosion inhibitor for cold rolled steel in hydrochloric acid Corros. Sci. 51 2009 569 574 [54] W.J. Lorenz F. Mansfeld Determination of corrosion rates by electrochemical DC and AC methods Corros. Sci. 21 1981 647 672 [55] M. Lagrenée B. Mernari M. Bouanis M. Traisnel F. Bentiss Study of the mechanism and inhibiting efficiency of 3,5-bis(4-metylthiophenyl)-4H-1,2,4-triazole on mild steel corrosion in acidic media Corros. Sci. 44 2002 573 588 [56] R.M. Saleh A.M. Shams El Din Efficiency of organic acids and their anions in retarding the dissolution of aluminium Corros. Sci. 12 1972 689 697