Corrosion Behavior of Aluminum in Dilute Acetic Acid Solution Simulating Cooling Water in HVDC Transmission
Peng Zhang,Hao Zhang,Yinsheng Xu,Huixi Li,Jinxiao Liu,Youping Fan,Shengping Wang
DOI: https://doi.org/10.20964/2022.03.05
IF: 1.541
2022-01-01
International Journal of Electrochemical Science
Abstract:The concentration, temperature effect and thermodynamic activation energy of aluminum corrosion in dilute acetic acid solution were explored by the polarization curve and the electrochemical impedance spectroscopy. With the increase of concentration and solution temperature of acetic acid solution, the corrosion resistance and charge transfer impedance of aluminum decreased. From 0 mM to 1.00 mM of acetic acid solution concentration, the corrosion potential, corrosion current density, anodic Tafel slope and charge transfer impedance of aluminum corrosion at 25 degrees C changed from -1.316 V, 0.207 mu A cm(-2), 5.581 V dec(-1), 10.890 k Omega cm(-2) to -1.141 V, 0.525 mu A cm(-2), 4.264 V dec(-1), 7.344 kd(2) cm(-2). And with the solution temperature increase from 25 degrees C to 55 degrees C, the corrosion potential, corrosion current, anodic Tafel slope and charge transfer impedance of aluminum in 0.1 mM acetic acid solution changed from 1.248 V, 0.337 mu A cm(-2), 5.387 V dec(-1), 9.590 k Omega cm(-2) to -1.046 V, 1.651 mu A cm(-2), 5.031 V dec(-1), 1.633 k Omega cm(-2). The aluminum corrosion in dilute acetic acid solution was a transition chemical reaction of four processes (diffusion -> surface adsorption -> surface reaction -> desorption).