Abstract:The stress corrosion cracking (SCC) susceptibility of 7A04 high strength aluminum alloy in 3.5% (mass fraction) NaCl solution and the Ce3+ inhibition of SCC were investigated by slow stress rate test(SSRT), using constant current polarization, electrochemical noise (ECN) and electrochemical impedance spectroscopy (EIS) techniques. The inhibition mechanism of Ce3+ ions on the initiation and propagation of cracking was also analyzed. The results indicate that both anodic and cathodic galvanostatic polarizations can accelerate the SCC of 7A04, the former increases anodic dissolution but the latter accelerates hydrogen embrittlement of crack tip. SCC susceptibility of 7A04 can be reduced effectively by the addition of cerium ions, the fracture time is delayed and slowed down, but only during the initiation other than the propagation stage of cracking. Ce3+ ions can restrain the initiation of metastable pitting on the surface of 7A04 specimen, which therefore increase the induction time of the cracking since that the micro pits are usually the source of cracking. However, once the crack begins to propagate or the specimen is notched, the addition of cerium ions can rarely inhibit the cracking process. This is possibly attributed to that the radius of Ce3+ ion is too large to diffuse into the crack tip or it is hard to form protective CeO2 layer, Ce3+ ion therefore fails to rehabilitate the active alloy at the crack tip and further reduce the SCC developing rate of 7A04. SEM also indicates that the crack initiation of smooth 7A04 specimens is mainly induced by metastable or stable pits.

Corrosion Inhibition of Aluminium Anode by Cecl3 in Simulated Seawater

Corrosion Inhibiton Mechanism of Cerium(III) for Aluminum Alloy

CORROSION INHIBITION MECHANISM OF CERIUM(Ⅲ) FOR ALUMINUM ALLOY

Corrosion resistance of anodically oxidized LY12 aluminum alloy after modification with cerium nitrate and silane

The Effect of Cecl3 As an Inhibitor on the Localized Corrosion of Aa2024-T3 As A Function of Temperature

Localized Corrosion and Corrosion Inhibitor of Al-alloy AA6061 Beneath Electrolyte Layers

The Solute Cerium to Enhance Corrosion Resistance of Magnesium Anode in 3.5% NaCl Solution

Influence of Cerium on Microstructures and Electrochemical Properties of Al-Mg-Sn-Hg Anode Materials for Seawater Battery

Influence of sodium alginate and chromate on aluminum corrosion in simulated HVDC cooling water

Synergistic Effect Between Glutamic Acid and Rare Earth Cerium (III) As Corrosion Inhibitors on AA5052 Aluminum Alloy in Neutral Chloride Medium

Corrosion Inhibition Mechanism of Rare Earth Metal on LC4 Al Alloy with Split Cell Technique

Corrosion Inhibition of 3003 Aluminum Alloy by Cerium Chloride-Sodium Nitrite Blend in Flue Gas Condensate

Effect of Ce on corrosion behaviors of aluminum in 3.5% NaCl solution

Study of Corrosion Inhibition of Coupled Al2Cu–Al and Al3Fe–Al by Cerium Cinnamate Using Scanning Vibrating Electrode Technique and Scanning Ion-Selective Electrode Technique

Cerium-based Chemical Conversion Coating on Aluminum Alloy to Inhibits Corrosion in Chloride Solution

Inhibitive effect of quaternary ammonium-type surfactants on the self-corrosion of the anode in alkaline aluminium-air battery

Inhibition Of Ce3+ On Stress Corrosion Crack Of High Strength Aluminum Alloy

An Investigation of Inhibition Mechanism of Cerium for Aluminum Alloy 2024-T3

Corrosion Protection Of Aluminium Alloy 2024-T3 In 0.05 M Nacl By Cerium Cinnamate

Effect of cerium acetate and L-glutamic acid as hybrid electrolyte additives on the performance of Al–air battery

Inhibition of Galvanic Corrosion in Al/Cu Coupling Model by Synergistic Combination of 3-Amino-1,2,4-triazole-5-thiol and Cerium Chloride