Hot deformation behavior of a CuAlMn shape memory alloy

Pang Yong,Xiao Zhu,Jia Yanlin,Zhang Rui,Yi Jiang,Qiu Wenting,Li Zhou

DOI: https://doi.org/10.1016/j.jallcom.2020.156161

IF: 6.2

2020-12-01

Journal of Alloys and Compounds

Abstract:<p>The hot deformation behaviors of single- and two-phase CuAlMn shape memory alloy were studied. Isothermal compression tests were conducted at different temperatures from 400<span class="math"><math>°C</math></span> to 800<span class="math"><math>°C</math></span> and various strain rates from 0.001/S to 1/S. At the temperature below 500<span class="math"><math>°C</math></span>, CuAlMn alloy had a two-phase microstructure (FCC <span class="math"><math>α</math></span> phase + <span class="math"><math>L21</math></span> <span class="math"><math>β</math></span> phase); while at the temperature higher than 550<span class="math"><math>°C</math></span>, the alloy had a single <span class="math"><math>β</math></span> phase structure. The flow stress curves showed the stress drop for all samples, indicating a dynamic recrystallization (DRX) feature of the alloy. The local minimum value of stress drop appeared at 500<span class="math"><math>°C</math></span>. The thermal active energy (<span class="math"><math>Q</math></span>) were calculated to be <span class="math"><math>418.7 kJ mol−1</math></span> for <span class="math"><math>α+β</math></span> alloy at 400–500<span class="math"><math>°C</math></span> and <span class="math"><math>219.7 kJ mol−1</math></span> for <span class="math"><math>β</math></span> alloy at 550–800<span class="math"><math>°C</math></span>, respectively. The artificial neural network (ANN) model showed a high precision to predict the flow stress of the studied alloy at a wide range of temperature. Based on the dynamic material model (DMM) theory, the processing map of the alloy that consists of the contour lines of the power dissipation factor, <span class="math"><math>η</math></span>, and the instability criteria was established. The grains were refined to a micron level and DRX of <span class="math"><math>α</math></span> phase occurred during the deformation between 400–500<span class="math"><math>°C</math></span> at the low strain rate. The hot deformation behaviors of the alloy at the low temperature (400–450<span class="math"><math>°C</math></span>) mainly depended on the deformation of <span class="math"><math>α</math></span> phase. The optimum deformation parameters for the single-phase CuAlMn alloys were 750–800<span class="math"><math>°C</math></span>/0.1–1 s⁻¹.</p>

materials science, multidisciplinary,chemistry, physical,metallurgy & metallurgical engineering