Abstract:Semipolar III-nitrides have attracted great attention due to their weak polarization field for optoelectronic devices. High-quality AlN is a perfect template in the epitaxial growth of AlGaN-based ultraviolet optical devices. In this work, (112̅2) semipolar AlN was grown on m-plane sapphire by the hierarchical growth mode. A high density of extended defects due to the lattice mismatch and anisotropic growth rate is identified in the as-grown AlN thin film. The influence of thermal annealing and AlN regrowth on the evolution of stacking faults and dislocations in AlN was thoroughly investigated by high-resolution transmission electron microscopy. Extending defects turned into partial dislocations after high-temperature treatment, by which the stacking faults were buried inside the AlN template, incapable of propagating into the AlN regrowth layer. As a result, the AlN regrowth layer exhibits superior crystalline quality. However, compressive strain is found after high-temperature annealing (HTA), which introduces new defects in the AlN regrowth layer. Strain management is demonstrated to be crucial for the quality control of the AlN layer. Overall, high-temperature annealing and regrowth processes proved to be stable and repeatable techniques in the realization of high-efficiency semipolar UV semiconductor devices.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acs.cgd.1c00086?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acs.cgd.1c00086</a>.In-plane crystallographic relationship and RSM of AlN and sapphire; HRTEM and IFFT analysis of defect-free AlN regions; and summarized lattice distance and strain at each processing stage (<a class="ext-link" href="/doi/suppl/10.1021/acs.cgd.1c00086/suppl_file/cg1c00086_si_001.pdf">PDF</a>).This article has not yet been cited by other publications.

2-inch semi-polar (11̄2) AlN templates prepared by high-temperature hydride vapor phase epitaxy

Improved Surface Morphology and Crystalline Quality of Semi-Polar (112‾2) AlN Epilayer with Dual Moderate-Temperature-grown AlN Interlayers

Improved surface morphology and crystalline quality of semi-polar ( 11 2 ̅ 2 ) AlN epilayer with dual moderate-temperature-grown AlN interlayers

The Structural Evolution of Semipolar (11−22) Plane AlN Tem-Plate on m-Plane Sapphire Prepared by Sputtering and High Temperature Annealing

Preparation Of Aln Film Grown On Sputter-Deposited And Annealed Aln Buffer Layer Via Hvpe

Three-step Growth of AlN Films on Sapphire Substrates by Metal Nitride Vapor Phase Epitaxy

AlN Thin Film Grown on Different Substrates by Hydride Vapor Phase Epitaxy

Epitaxial AlN film with improved quality on Si (111) substrates realized by boron pretreatment via MOCVD

The In-Plane-Two-Folders Symmetric a-Plane AlN Epitaxy on r-Plane Sapphire Substrate

Preparation of high-quality thick AlN layer on nanopatterned sapphire substrates with sputter-deposited annealed AlN film by hydride vapor-phase epitaxy

Nucleation and growth of (10 ͞ 11) semi-polar AlN on (0001) AlN by Hydride Vapor Phase Epitaxy

AlN Thin Films Grown on Different Substrates by Metal Nitride Vapor Phase Epitaxy

Epitaxial Growth of 2 Inch Diameter Homogeneous Aln Single-Crystalline Films by Pulsed Laser Deposition

High quality non-polar a-plane AlN template grown on semi-polar r-plane sapphire substrate by three-step pulsed flow growth method

High Quality AlN Film Grown on a Nano-Concave-circle Patterned Si Substrate with an AlN Seed Layer

The In-Plane-Two-Folders Symmetric <i>a</i>-Plane AlN Epitaxy on <i>r</i>-Plane Sapphire Substrate

Four-inch High Quality Crack-Free AlN Layer Grown on a High-Temperature Annealed AlN Template by MOCVD

Toward Φ56 mm Al-Polar AlN Single Crystals Grown by the Homoepitaxial PVT Method

4-inch 11 μm high-quality AlN thick films grown on nanopatterned sapphire substrates

Annihilation and Regeneration of Defects in (112̅2) Semipolar AlN via High-Temperature Annealing and MOVPE Regrowth

Homoepitaxy Growth of High‐Quality AlN Film on MOCVD AlN Template by Hydride Vapor Phase Epitaxy