Abstract:Mesoporous carbon materials with ultra-thin carbon pore walls and highly dispersed Ni nanoparticles have been successfully prepared by using two different SBA-15 silicas as hard templates and 2,3-dihydroxynaphthalene (DHN) as a carbon precursor. The nickel precursor was a concentrated nickel nitrate hexahydrate [Ni(NO3)(2)center dot 6H(2)O] solution in 2-propanol, which was added to the carbon-silica nanocomposite prior to thermal treatment. The samples studied were analyzed by thermogravimetry (TG), nitrogen adsorption at -196 degrees C, powder X-ray diffraction (XRD), Raman spectroscopy, scanning and transmission electron microscopy (STEM), and in situ electron diffraction X-ray spectroscopy (EDX). While TG analysis revealed carbon contents lower than 30 wt.-%, nitrogen adsorption provided information about the homogeneity of the carbon thin film deposited onto the mesopore walls of the ordered silica templates SBA-15. The templates, carbon-silica nanocomposites, and carbon inverse replicas with nickel nanoparticles exhibit uniform pores, high surface areas, and large pore volumes. Partially graphitic carbon was identified by the presence of a characteristic G band in the Raman spectra, whereas the diffraction peak attributed to the stacking of graphene planes was not observed by powder XRD. The presence of ordered domains in the carbon materials studied was confirmed by small angle XRD and STEM imaging. In addition, the STEM images revealed that the nickel nanoparticles are uniform in size, ca. 3 nm, and are homogeneously dispersed on the tubular carbon walls. A few larger clusters of nickel, ca. 60 nm, present on the external surface, were identified by powder XRD as metallic Ni. The in situ EDX revealed that the small nanoparticles are largely composed of Ni with traces of NiO. Similar nanoparticle dispersions have been reported only for Ni-containing multiwalled carbon nanotubes (CNTs), whereas previously reported ordered mesoporous carbon materials, CMK-3, possess larger Ni/NiO nanoparticles. ((C) Wiley-VCH Verlag GmbH & Co. KGaA, 69451 Weinheim, Germany, 2009)

Site selective synthesis of in situ Ni filled multiwalled carbon nanotubes using Ni(salen) as a catalyst source

Lithographically defined site-selective growth of Fe filled multi-walled carbon nanotubes using a modified photoresist

Carbon nanotube synthesis from propane decomposition on a pre-treated Ni overlayer

Growth and Characterization of Multi-Walled Carbon Nanotubes using Chemical Vapor Deposition

The effect of Fe and Ni catalysts on the growth of multiwalled carbon nanotubes using chemical vapor deposition

Synthesis of Well-Aligned Multiwalled Carbon Nanotubes on Ni Catalyst Using Radio Frequency Plasma-Enhanced Chemical Vapor Deposition

Mesoporous Carbon Materials with Ultra‐Thin Pore Walls and Highly Dispersed Nickel Nanoparticles

In Situ Synthesis of Multiwalled Carbon Nanotubes over Lanio3 As Support of Cobalt Nanoclusters Catalyst for Catalytic Applications

Large-Scale and Solvent-Free Synthesis of Magnetic Bamboo-Like Nitrogen-Doped Carbon Nanotubes with Nickel Active Sites for Photothermal-Driven CO 2 Fixation

Carbon Nanotubes Filled with Metallic Nanowires

<i>In Situ</i> Filling of Fe/Ni Oxide Nanowire into Carbon Nanotubes Doped with Nitrogen in CH<sub>4</sub>/H<sub>2</sub>/Air Plasma

The Role of the Catalytic Particle in the Growth of Carbon Nanotubes by Plasma Enhanced Chemical Vapor Deposition

One-Pot Pyrolysis Method to Fabricate Carbon Nanotube Supported Ni Single-Atom Catalysts with Ultrahigh Loading

Synthesis of multi-walled carbon nanotubes on nichrome and nickel by using rapid thermal processing furnace

Synthesis of carbon nanotubes with Ni/CNTs catalyst

In situ growth of N-doped carbon nanotubes from the products of graphitic carbon nitride etching by nickel nanoparticles

In-situ filling of Fe/Ni oxide nanowire into carbon nanotubes doped with nitrogen in CH4/H2/air plasmas

Synthesis Of Nickel Nanoparticles And Carbon Encapsulated Nickel Nanoparticles Supported On Carbon Nanotubes

Synthesis,Characterization and Performance of Helical Carbon Nanotubes

Large-scale Synthesis of Uniform Nanotubes of a Nickel Complex by a Solution Chemical Route.

Nitrogen-doped carbon nanotubes synthesized with carbon nanotubes as catalyst