Magnetic properties and anomalous Hall effect of Mn3Sn thin films controlled by defects and ferroelectric 0.7Pb(Mg1/3Nb2/3)O3–0.3PbTiO3 substrate

Zhong-Ping Zhao,Qi Guo,Feng-Hua Chen,Ke-Wei Zhang,Yong Jiang

DOI: https://doi.org/10.1007/s12598-020-01673-1

IF: 6.318

2021-02-06

Rare Metals

Abstract:<p class="a-plus-plus">Noncollinear antiferromagnetic Mn<sub class="a-plus-plus">3</sub>Sn films have received much attention due to their potential applications in antiferromagnetic spintronic devices. In this work, single-phase polycrystalline antiferromagnetic Mn<sub class="a-plus-plus">3</sub>Sn thin films were successfully prepared by magnetron sputtering. The defects in the thin films were regulated by adjusting the sputtering power. The relationship among the films structure, the anomalous Hall effect (AHE) and the defects was investigated. High defect concentration in the Mn<sub class="a-plus-plus">3</sub>Sn films led to large room temperature ferromagnetic moments. The maximum saturation magnetization reached up to ~ 16 kA·m<sup class="a-plus-plus">−1</sup> (36 mμ<sub class="a-plus-plus">B</sub>/Mn), which was much larger than the values reported in literatures. The coercive field of 38 mT was obtained in a high-quality Mn<sub class="a-plus-plus">3</sub>Sn film, which effectively reduced the flipping magnetic field. Moreover, the anomalous Hall resistance and coercive field of the Mn<sub class="a-plus-plus">3</sub>Sn films prepared on the ferroelectric substrates were manipulated through an applied electric field, indicating that the piezoelectric stress has a great influence on the nonzero Berry curvature of the triangular spin structure in the antiferromagnetic materials. These results will promote the potential application of Mn<sub class="a-plus-plus">3</sub>Sn in high-density and low-power antiferromagnetic spintronic devices.</p>

materials science, multidisciplinary,metallurgy & metallurgical engineering