Abstract:In this work, we successfully report the design and synthesis of rod-like CoAl2O4/halloysite hybrid pigment from zeolitic imidazolate framework-67 (ZIF-67, a Co-based MOF) and tubular halloysite via a facile two-step route for the first time. The as-prepared nanostructures were thoroughly characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM), transmission electron microscopy (TEM), Fourier transform infrared reflection (FTIR Spectroscopy), thermogravimetric and differential scanning calorimetry (TG-DSC), X-ray photoelectron spectrometer (XPS), ultraviolet–visible spectrometry (UV–vis) and CIE L* a* b* colorimetric method. XRD patterns indicated that the presence of CoAl2O4 spinel was observed at various temperatures ranging from 800 to 1100 °C. The SEM and TEM images showed that the nano-pigment has a rod-like hybrid structure composed of nano CoAl2O4 particles and SiO2. The color performance of the fabricated pigments was evaluated and given suitable color coordinates (L* = 44.72, a* = −14.40, b* = −37.83) and (L* = 42.57, a* = −7.68, b* = −41.14) at the calcination temperature of 1100 °C for 2 h and 3 h, respectively. The mechanism study indicated that these composites were formed by Co3O4 derived of ZIF-67 as highly active cobalt source and Al2O3 decomposed from halloysite substrate as aluminum source. In addition, the corrosion resistance test showed that the CoAl2O4 composites retain crystalline stability, almost no color deviation in CIE chromatic system even after 1 M HCl leaching. Furthermore, the CoAl2O4/halloysite exhibited excellent thermal and suspension stability, which indicated it could be a promising candidate for ceramic glazes and water-borne coatings. These findings provide insight into a new strategy for the synthesis of clay mineral-based ceramic pigment.

Synthesis of high color performance V-ZrSiO4 blue pigment with low doping amount via inorganic sol–gel route

Synthesis and chromatic properties of V-doped and V/Y-codoped ZrO2 yellow pigments

Synthesis, Characterization and Application of Submicron ZrSiO4 Powder Via Sol-Gel-microemulsion-hydrothermal Method

Ultrafine V-ZrSiO4 pigment prepared by a bottom-up approach: Particle size evolution and chromatic properties

The Preparation and Properties of Zircon—Vanadium Blue Ceramic Pigment

Synthesis and chromatic properties of high color performance Prx-ZrSiO4 (x = 0–0.1) yellow pigment

Preparation of Ultrafine Spherical Pr-ZrSiO 4 Pigment by Sol-Gel-Microemulsion Method

Non-solvent displacement nonaqueous precipitation method for core-shell materials preparation: Synthesis of C@ZrSiO4 black pigment

Synthesis and Chromatic Properties of Zircon Encapsulated Ceramic Black Pigment with Carbon Sphere As Carbon Source

Effective Synthesis of Green Nano‐sized Ceramic Pigments by Co‐doping Zn2+, Cr3+ and Sm3+ into the Cobalt‐aluminate

Preparation and Thermochromic Properties of Sol-Gel-derived Zr-doped VO 2 Films

Synthesis and properties of novel blue zirconia ceramic based on Co/Ni-doped BaAl12O19 blue chromophore

Synthesis of an Intensive Blue Pigment with Low Cobalt Content

Preparation and Characterization of Black Zirconia Ceramics by Black Color Spinel Pigment

Synthesis of zircon pigments from rice husk ash and their performance in ceramic glaze

Fabrication of Blue-Colored Zirconia Ceramics via Heterogeneous Nucleation Method

Synthesis and characterization of (Pr, Ce)‐ZrSiO 4 ceramic pigments: The properties of the pigments and the effect of Ce

Novel fabrication of rod-like CoAl2O4/halloysite hybrid pigment derived from Co-MOF/nano-clay and mechanism exploration

Simultaneous precipitation of Zr4+ and Y3+ ions induced refinement of precursors and powders in fabrication of Zr4+ doped Y2O3 transparent ceramics

High near-infrared reflectance Bi<sub>2</sub>O<sub>3</sub>-ZnO-CaO yellow pigment system

Preparation, characterization and coloring mechanism of 3D printed colorful ZrO 2 ceramics parts