Abstract:OBJECTIVE:To evaluate the colouration of zirconia ceramic by adding three kinds of rare earth oxides. The influence of the pigments concentration on the mechanical properties and the microstructure was also analyzed.METHODS:Added different concentrations of CeO(2), Er(2)O(3) and Pr(6)O(11) in tetragonal zirconia poly crystals stabilized with 3 mol% yttria (3Y-T2P) powder, compacted at 200 MPa using cold isostatic pressure, and sintered to 1 400 degrees C. The heating rate was 150 degrees C/h and the dwelling time was 2 hours. The chromaticity of sintered bodies was measured with chroma meter. The relative density, hardness, flexure strength and fracture toughness were investigated as well. The phase stability of the colorized and pure zirconia was evaluated by X-ray diffraction (XRD) using an automated diffractometer. The microstructures of the specimens were evaluated by scanning electron microscope (SEM).RESULTS:Several kinds of color achieved by the different pigments praseodym oxide, cerium oxide and erbium oxide were presented in the CIELab system. The a* value increased with the added amount of Er(2)O(3), while b* value rose with the increasing amount of CeO(2) and Pr(6)O(11). However, three pigments failed to decrease L* value and the sintered body appeared too bright. Adding three pigments influenced flexure strength of zirconia ceramic significantly, but had little influence on the hardness and fracture toughness. Microscopy revealed the relationship between the porosity and shapes of grains was correlated to strength of the diphase ceramics. No additional phase could be detected by XRD, except t-ZrO(2) in all colorized samples after sintering at 1 400 degrees C for 120 min.CONCLUSIONS:Zirconia ceramic can be colorized by CeO(2), Er(2)O(3), and Pr(6)O(11). Pigments even in a small amount influence the mechanical properties of the colorized zirconia material, which necessitates further investigation.

Synthesis and chromatic properties of V-doped and V/Y-codoped ZrO2 yellow pigments

Synthesis of high color performance V-ZrSiO4 blue pigment with low doping amount via inorganic sol–gel route

Synthesis and chromatic properties of high color performance Prx-ZrSiO4 (x = 0–0.1) yellow pigment

Synthesis, Characterization and Application of Submicron ZrSiO4 Powder Via Sol-Gel-microemulsion-hydrothermal Method

Pigments based on Er2O3-Al2O3: Preparation and colouring performance in zirconia ceramics

Preparation and Thermochromic Properties of Sol-Gel-derived Zr-doped VO 2 Films

The Preparation and Properties of Zircon—Vanadium Blue Ceramic Pigment

Effective Synthesis of Green Nano‐sized Ceramic Pigments by Co‐doping Zn2+, Cr3+ and Sm3+ into the Cobalt‐aluminate

Ultrafine V-ZrSiO4 pigment prepared by a bottom-up approach: Particle size evolution and chromatic properties

[Effect of Three Kinds of Rare Earth Oxides on Chromaticity and Mechanical Properties of Zirconia Ceramic].

Synthesis and Chromatic Properties of Zircon Encapsulated Ceramic Black Pigment with Carbon Sphere As Carbon Source

Synthesis and Characterization of Zn1-xMnxO Yellow Pigment with High Near-Infrared Reflectance

High near-infrared reflectance Bi<sub>2</sub>O<sub>3</sub>-ZnO-CaO yellow pigment system

RESEARCH PROGRESS IN YELLOW PIGMENTS OF RARE EARTH

Simultaneous precipitation of Zr4+ and Y3+ ions induced refinement of precursors and powders in fabrication of Zr4+ doped Y2O3 transparent ceramics

High Near-Infrared Reflectance Zn1-xMnxO Yellow Pigment Prepared and Properties by Co-Precipitation Method

Synthesis and characterization of (Pr, Ce)‐ZrSiO 4 ceramic pigments: The properties of the pigments and the effect of Ce

Synthesis and Characterization of Chromium Doped Y3Al5O12 Compound Pigment

Research on the Coloration of Dental Zirconia

The Color of Fe<sub>2</sub>O<sub>3</sub> and Bi<sub>2</sub>O<sub>3</sub> Pigmented Dental Zirconia Ceramic

[Effect of Five Kinds of Pigments on the Chromaticity of Dental Zirconia Ceramic].