Abstract:Dental multilayer zirconia ceramics are attractive materials for restorative dentistry because they offer significant esthetic advantages over monolithic, white, or monocolored zirconia. They enable anatomical adjustments in dental prostheses, making them more similar to natural teeth. New categories of dental ceramics have been developed using varying translucency and color within the same piece to meet aesthetic requirements. This technique employs zirconia with different yttria (Y 2 O 3 ) contents to achieve varying levels of translucency. This study investigated two types of dental ceramics based on multilayer zirconia, correlating their mechanical properties, translucency, and color variations concerning their application in dental prostheses. Two types of multilayer zirconia pre-sintered blocks with different Y 2 O 3 content were examined: 1) blocks with a Y 2 O 3 gradient chemical composition between 3 mol.% and 4 mol.%, named M3-4YSZ; 2) blocks with a Y 2 O 3 gradient chemical composition between 4 mol.% and 5 mol.%, named as M4-5YSZ Samples were cut in cross-section to separate the layers based on Y 2 O 3 content and color and were then sintered at 1530 °C for 2 hours. The sintered samples were characterized by relative density, crystalline phases, microstructure, Vickers hardness, fracture toughness (K IC ), and optical properties (color and contrast ratio). Fully dense ceramics were obtained after sintering. Layers containing a greater amount of Y 2 O 3 in the zirconia matrix have a higher content of the ZrO 2 cubic phase, while layers with a lower content of Y 2 O 3 in the matrix are predominantly tetragonal ZrO 2 . No statistical variation in hardness was observed depending on the layers of the material. However, fracture toughness values showed significant statistical variations, with an increase in the tetragonal phase content responsible for the increase in fracture toughness. K IC in M3-4YSZ samples varied between 3.63 and 7.73 MPa.m 1 /2 , while M4-5YSZ samples ranged from 2.70 to 5.65 MPa.m 1/2 . The smooth and gradual variations in color and translucency observed between the layers of the two groups of dental ceramics studied indicate stability and homogeneity between the layers, contributing significantly to esthetic effects in dental applications.

The Color of Fe<sub>2</sub>O<sub>3</sub> and Bi<sub>2</sub>O<sub>3</sub> Pigmented Dental Zirconia Ceramic

Effect of Pigmentation on the Mechanical Properties and Microstructure of Dental 3Y-TZP Ceramics

Production and properties of tooth-colored yttria stabilized zirconia ceramics for dental applications

Research on the Coloration of Dental Zirconia

Bi-colored zirconia as dental restoration ceramics

Effects of Aging on the Mechanical Properties of Dental Pigmented 3Y-Tzp Ceramics

Color Reproduction And Shade Stability Of Zirconia Ceramics

High Strength and Toughness in Chromatic Polymer-Infiltrated Zirconia Ceramics.

Pigments based on Er2O3-Al2O3: Preparation and colouring performance in zirconia ceramics

Study of colored on the microwave sintering behavior of dental zirconia ceramics

Synthesis of Coloured Dental Zirconia Ceramics and Their Mechanical Behaviors

Effect of metal elements in coloring liquids used in the infiltration method on the physical properties of zirconia

The influence of colored zirconia on the optical properties of all-ceramic restorations

Conventional sintering of nano-crystalline Yttria-Stabilized Zirconia enables high-strength, highly translucent and opalescent dental ceramics

In vitro evaluation of tooth-colored yttria stabilized zirconia ceramics

Coloring Multilayer Zirconia May Affect Its Optical and Mechanical Properties

Mechanism underlying ultraviolet-irradiation-induced discoloration of dental zirconia ceramics stabilized with 3 and 5 mol% yttria

Mechanical and optical properties of multilayer yttria-stabilized zirconia for dental prostheses

Production and characterization of self-colored dental zirconia blocks

Direct colour printing on zirconia using 222 nm UV-C photons

New zirconia-based materials for dental applications. Structural, morphological and histological evaluation

The Color of Fe&lt;sub&gt;2&lt;/sub&gt;O&lt;sub&gt;3&lt;/sub&gt; and Bi&lt;sub&gt;2&lt;/sub&gt;O&lt;sub&gt;3&lt;/sub&gt; Pigmented Dental Zirconia Ceramic