Production and properties of tooth-colored yttria stabilized zirconia ceramics for dental applications

Melis Kaplan,Jongee Park,Soo Young Kim,Abdullah Ozturk

DOI: https://doi.org/10.1016/j.ceramint.2017.10.211

IF: 5.532

2018-02-01

Ceramics International

Abstract:Dense zirconia stabilized with 3mol% yttria ceramics were produced in disc shape by first cold isostatically pressing at 100MPa and then sintering at 1450°C at ambient laboratory conditions. Coloring was accomplished by immersion the discs in NiCl2, MoCl3, and NiCl2 + MoCl3 solutions for 5, 30, and 60s. Different concentrations (0.1, 0.25, and 0.5wt%) were applied to get the color of natural tooth. The density, color, microhardness, fracture toughness, compressive strength, and wear rate of the discs were measured to evaluate the suitability of the colored discs for dental applications. Color assessments were made by measuring CIE Lab L * , a * , b * , and ΔE * values. Low temperature degradation of the samples was evaluated by aging sensitivity tests in autoclave for 2, 4, and 6h. Results have shown that color produced depends on the kind and concentration of the colorant solution while time of immersion has no significant effect on coloring process. Coloring solutions containing 0.1 and 0.25wt% MoCl3 provided clinically acceptable color with the ΔE* value ranging from 5.16 to 6.42 for dental applications.

materials science, ceramics