Abstract:OBJECTIVE:To evaluate the colouration of zirconia ceramic by adding three kinds of rare earth oxides. The influence of the pigments concentration on the mechanical properties and the microstructure was also analyzed.METHODS:Added different concentrations of CeO(2), Er(2)O(3) and Pr(6)O(11) in tetragonal zirconia poly crystals stabilized with 3 mol% yttria (3Y-T2P) powder, compacted at 200 MPa using cold isostatic pressure, and sintered to 1 400 degrees C. The heating rate was 150 degrees C/h and the dwelling time was 2 hours. The chromaticity of sintered bodies was measured with chroma meter. The relative density, hardness, flexure strength and fracture toughness were investigated as well. The phase stability of the colorized and pure zirconia was evaluated by X-ray diffraction (XRD) using an automated diffractometer. The microstructures of the specimens were evaluated by scanning electron microscope (SEM).RESULTS:Several kinds of color achieved by the different pigments praseodym oxide, cerium oxide and erbium oxide were presented in the CIELab system. The a* value increased with the added amount of Er(2)O(3), while b* value rose with the increasing amount of CeO(2) and Pr(6)O(11). However, three pigments failed to decrease L* value and the sintered body appeared too bright. Adding three pigments influenced flexure strength of zirconia ceramic significantly, but had little influence on the hardness and fracture toughness. Microscopy revealed the relationship between the porosity and shapes of grains was correlated to strength of the diphase ceramics. No additional phase could be detected by XRD, except t-ZrO(2) in all colorized samples after sintering at 1 400 degrees C for 120 min.CONCLUSIONS:Zirconia ceramic can be colorized by CeO(2), Er(2)O(3), and Pr(6)O(11). Pigments even in a small amount influence the mechanical properties of the colorized zirconia material, which necessitates further investigation.

Synthesis and properties of novel blue zirconia ceramic based on Co/Ni-doped BaAl12O19 blue chromophore

Fabrication of Blue-Colored Zirconia Ceramics via Heterogeneous Nucleation Method

Synthesis and optical properties of Ni/Co/Cr doped BaMg6Ti6O19

One-step hydrothermal synthesis of yttria-stabilized tetragonal zirconia polycrystalline nanopowders for blue-colored zirconia-cobalt aluminate spinel composite ceramics

Fabrication of Colored Zirconia Ceramics Doped with the Spinelvia Heterogeneous Nucleation Method

Effective Synthesis of Green Nano‐sized Ceramic Pigments by Co‐doping Zn2+, Cr3+ and Sm3+ into the Cobalt‐aluminate

Environmental Blue CoAl2O4 Pigment Co-Doped by Zn2+ and Mg2+: Synthesis, Structure and Optical Properties

Preparation and Characterization of Black Zirconia Ceramics by Black Color Spinel Pigment

Synthesis, properties and applications of novel inorganic yellow pigments based on Ni-doped Al2TiO5

Tailoring Multifunctional Performance of Dy-doped (ba0.85ca0.15)(zr0.1ti0.9)o3 Ceramics Via Optimizing Ceramic Processing

Preparation and research of new black zirconia ceramics

Pigments based on Er2O3-Al2O3: Preparation and colouring performance in zirconia ceramics

Synthesis of Coloured Dental Zirconia Ceramics and Their Mechanical Behaviors

Color‐tunable and White Emission of Tm3+ Doped Transparent Zinc Silicate Glass‐ceramics Embedding ZnO Nanocrystals

Preparation and characterization of inverse spinel green nano-ceramic pigment

Preparation and properties of black Ti-doped zirconia ceramics

Synthesis and optical properties of Mn-doped Ba3Al2O6 intense blue oxides

Synthesis of high color performance V-ZrSiO4 blue pigment with low doping amount via inorganic sol–gel route

Metal Ions Doped Complex Cobalt Blue Pigment Research

Synthesis and chromatic properties of V-doped and V/Y-codoped ZrO2 yellow pigments

[Effect of Three Kinds of Rare Earth Oxides on Chromaticity and Mechanical Properties of Zirconia Ceramic].