Abstract:Purpose The purpose of this paper is to conduct the directed synthesis of blue-colour aluminate spinel pigments based on spent aluminium–cobalt–molybdenum (ACM) catalyst and to study peculiar features of mineral formation processes and changes in their colour indices depending on composition and firing temperature. Design/methodology/approach Aluminate spinel ceramic pigments with specified colour indices were synthesised by directed formation of their mineral composition and identification of the most rational technological parameters of production. Mineral composition of synthesised pigments was evaluated by X-ray phase analysis. The colour indices of pigments and pigment-containing glaze coatings were studied on the comparator colour. The chemical resistance of pigments was determined by loss of their weight loss after boiling in 1 N hydrochloric acid solution and 1 N sodium hydroxide solution. Findings Peculiar features of formation of the mineral composition of aluminate spinel pigments based on the ACM catalyst were studied. The expediency of using magnesium and zinc oxides in their composition has been proved. It is found that for the formation of stable pigments of intense blue colour, a concentration of cobalt (II) oxide in the amount of 0.5 mol is sufficient, which is 23.1 Wt.%. The colour of such pigments is determined by the ratios of cobalt, magnesium and zinc aluminates, which form a spinel solid solution. Practical implications The use of developed aluminate spinel pigments provides obtaining of high-quality glass coatings of blue colour, in particular, for ceramics. Originality/value Aluminium oxide in the spent ACM catalyst is predominantly in the active form (of amorphous aluminium hydroxide and y-Al 2 O 3 ). This is a prerequisite for the use of this waste material as a complete substitute for chemically pure Al 2 O 3 in the technology of aluminate spinel pigments and reduction of their firing temperature. Besides, spent ACM catalyst already contains 5 Wt.% of expensive cobalt (II) oxide in the form of stable colour-bearing phase CoAl 2 O 4 .

Preparation and characterization of inverse spinel green nano-ceramic pigment

Effective Synthesis of Green Nano‐sized Ceramic Pigments by Co‐doping Zn2+, Cr3+ and Sm3+ into the Cobalt‐aluminate

Preparation and Characterization of Black Zirconia Ceramics by Black Color Spinel Pigment

Preparation of Submicron-Sized ZnFe2-xCrxO4 (x = 0.4, 0.8) Via a Two-Step Method and Evaluation of the Corresponding Ceramic Inks

Combustion Synthesis of ZnFe Cr O4 Nanocrystallites for Ceramic Digital Decoration

Preparation, Chromatic Properties Analysis and Proportioning Optimization of Co-Cr-Fe-Based Black Pigment

Preparation and characterization of Cr2O3-TiO2-Co2O3-ZnO green pigment

Synthesis and Characterization of Zn1-xCoxO Green Pigments with Low Content Cobalt Oxide

Effect of the nickel molar content on the preparation and properties of spinel-type black ceramic pigment by microwave processing from stainless steelmaking dust

Synthesis of High Near Infrared Reflection Wurtzite Structure Green Pigments Using Co-doped ZnO by Combustion Method

The Effect of Ni2+ Ions Substitution on Structural, Morphological, and Optical Properties in CoCr2O4 Matrix as Pigments in Ceramic Glazes

Synthesis and Characterization of Chromium Doped Y3Al5O12 Compound Pigment

Preparation and Characterization of Nanoscale Cobalt Blue Pigment for Ceramic Inkjet Printing by Sol-Gel Self-Propagating Combustion

Synthesis and characteristics of aluminate spinel ceramic pigments based on spent aluminium-cobalt-molybdenum catalyst

Sonochemical Synthesis and Characterization of Spinel CoAl2O4 Nanoparticles

Synthesis and Analysis of Zn-Substituted CoCr2O4 Spinel Oxide

Synthesis and Chromatic Properties of Zircon Encapsulated Ceramic Black Pigment with Carbon Sphere As Carbon Source

Environmental Blue CoAl2O4 Pigment Co-Doped by Zn2+ and Mg2+: Synthesis, Structure and Optical Properties

Study of the Synthesis of Brown Spinel Pigments for Porcelain Insulator

Synthesis and properties of novel blue zirconia ceramic based on Co/Ni-doped BaAl12O19 blue chromophore

Preparation and Characterization of Novel Nonstoichiometric Magnesium Aluminate Spinels