Abstract:In this study, a high-performance Mg–8Gd–2Y–1Zn–6Li (wt%) alloy having a TYS of 202 ± 2.6 MPa, UTS of 243 ± 2.1 MPa and EL of 10.7 ± 2.3% was successfully fabricated by casting, heat treatment and hot extrusion. The effects of intermetallic compounds on microstructure and mechanical properties were deeply investigated. The results show that the studied alloy consists of coarse deformed α-Mg grains with (0001) basal texture, fine recrystallized β-Li grains with (002) texture and three Mg3RE phase variants, which are bulk Mg3RE phase with a size range of 10–30 µm, spot Mg3RE phase with a size range of 1–2 µm and spherical Mg3RE phase with a size range of 0.3–1 µm, respectively. The spherical Mg3RE phase has a strong dispersion strengthening effect, while the bulk Mg3RE phase acts as crack resources and deteriorates the ductility. A novel island-like <math>β1R</math> phase (FCC, a = 0.78 nm) is found for the first time in the Mg-Gd-Li based alloys. It has a coherent <math>(1̅12)β1R</math>//<math>(101̅0)α</math> interface at the broad facet and a semi-coherent <math>(1̅11)β1R</math>//<math>(112̅0)α</math> interface at the end facet. The <math>β1R</math> phase transforms from <math>βH</math> phase at the semi-coherent interface by atomic shear of RE and Mg atoms. The <math>β1R</math> phase provides a significant precipitation strengthening effect to the studied alloy, while the dissolution of <math>β1R</math> phase results in the age-softening phenomenon. The high-performance of the studied alloy is mainly attributed to the α/β duplex structure, three Mg3RE phase variants, and <math>β1R</math> phase.

Microstructure and mechanical properties of Mg–GdH2 composite prepared by internal hydrogenation

Microstructure and Hydrogen Storage Characteristics of Nanocrystalline Mg+xwt% LaMg2Ni (x=0–30) Composites

Hydrogen desorption properties of the MgH2-AlH3 composites

Study on the Dehydrogenation Properties and Reversibility of Mg(Bh4)(2)-Alh3 Composite under Moderate Conditions

Microstructures And Hydrogen Desorption Properties Of The Mgh2-Alh3 Composite With Nbf5 Addition

Hydrogen Storage Properties of Mg+10% TiFe_(1-x)Cr_x(x=0,0.3) Multi-Phase Alloys

Microstructural Evolution in Graphene Nanoplatelets Reinforced Magnesium Matrix Composites Fabricated Through Thixomolding Process

Interfacial microstructure, mechanical properties and strengthening mechanism of Mg/Al bimetallic composites produced by a novel compound casting with the addition of Gd

Hydrogen Storage Behaviors and Microstructure of MF3 (m=ti, Fe)-doped Magnesium Hydride

Investigations on Microstructure and Mechanical Properties of Cast Mg-Gd-Y-Zn-Zr-Nd Alloy

High entropy alloys containing immiscible Mg and refractory elements: Synthesis, structure, and hydrogen storage properties

Improving hydrogen storage performance of Mg-based alloy through microstructure optimization

Influences of Gd on the Microstructure and Strength of Mg–4.5Zn Alloy

Effect of Gd content on microstructure and dynamic mechanical properties of solution-treated Mg−xGd−3Y−0.5Zr alloy

Unveiling the effect of Gd content on the dynamic recrystallization behavior and resultant mechanical property of magnesium

Microstructure and Mechanical Properties of As-Cast and Heat Treated Mg-15Gd-3Y Alloy

Insights into thermodynamic destabilization in Mg-In-D hydrogen storage system: A combined synchrotron X-ray and neutron diffraction study

Microstructures and mechanical properties of as-extruded Mg–8Gd–2Y–1Zn–6Li alloy

In Situ Observation of Microstructure and Precipitate Phase Transformation during the Solidification of Mg‐Containing GH3625 Alloy at Different Cooling Rates

Microstructure Evolution and Mechanical Properties of Mg-7Gd-3Y-1Nd-2Zn-0.5Zr Alloy During Two-Step Homogenization Heat Treatment

Microstructure of as-cast Mg-4.2Zn-0.8Y (at.%) alloys containing Gd