Hydrogen desorption properties of the MgH2-AlH3 composites

Haizhen Liu,Xinhua Wang,Yongan Liu,Zhaohui Dong,Hongwei Ge,Shouquan Li,Mi Yan

DOI: https://doi.org/10.1021/jp407018w

2014-01-01

Abstract:In this work, the hydrogen desorption properties of the novel Mg-Al-H hydrogen storage composites prepared by ball-milling the as-received magnesium hydride (MgH2) and the as-prepared aluminum hydride (AlH3) with different molar ratios (1:1, 1:0.5, and 1:0.25) are investigated systematically. Nonisothermal desorption measurements show that more than 7.51 wt % of hydrogen is released from the Mg-Al-H composites when they are heated from room temperature to 500 degrees C. Thermal analysis by differential scanning calorimeter (DSC) and hydrogen desorption spectrum by mass spectrometer (MS-H-2) are used synchronously to study the desorption process of the Mg-Al-H. The onset hydrogen desorption temperature of MgH2 in the MgH2 + AlH3 composite is dramatically reduced from 320 degrees C for the pure MgH2 to below 252 degrees C. The DSC/MS-H-2 and the X-ray diffraction (XRD) analyses show that the desorption of MgH2 in the Mg-Al-H composite is composed of two steps with the reaction between MgH2 and Al forming Mg17Al12 as the first step and the self-decomposition of the residual MgH2 as the second step. Isothermal desorptions show that the desorption kinetics of the MgH2 in the Mg-Al-H composite is significantly improved. The apparent activation energy for the desorption of MgH2 in the MgH2 + 0.25AlH(3) is reduced to 144.6 kJ/mol, which contributes to the improvement in the desorption kinetics of MgH2. The Johnson-Mehl-Avrami (JMA) kinetic studies indicate that the desorption kinetic model of MgH2 in the Mg-Al-H composite is different from the pure MgH2. Concerning the reversibility, under the conditions of 300 degrees C and 5 MPa H-2, MgH2 in the Mg-Al-H composite is almost fully recovered after absorption for 5 h while it is partially recovered for the pure MgH2. Among the samples studied, the MgH2 + 0.25AlH(3) composite exhibits the highest reversible hydrogen storage capacity of 6.10 wt % (H/M).