Hydrogen Absorption/desorption Properties of Li–Al–N–H Composite

Rugan Chen,Xinhua Wang,Jingkui Yang,Lou Xu,Lixin Chen,Shouquan Li,Hongwei Ge,Changpin Chen

DOI: https://doi.org/10.1016/j.matchemphys.2010.11.048

IF: 4.778

2011-01-01

Materials Chemistry and Physics

Abstract:Li3AlH6 and LiNH2 at a 1:3 molar ratio were mechanically milled to yield a Li–Al–N–H composite. The hydrogen storage properties of the composite were studied using thermogravimetry, differential scanning calorimetry, mass spectrometry, and X-ray diffraction. Addition of LiNH2 lowered the decomposition temperature of Li3AlH6. The Li–Al–N–H composite began to release hydrogen at around 110°C, which was 90°C lower than the initial desorption temperature of Li3AlH6. About 7.46wt% of hydrogen was released from the composite after heating from room temperature to 500°C. A total hydrogen desorption capacity of 8.15wt% was obtained after accounting for hydrogen released in the ball-milling process. The resulting dehydrogenated composite absorbed 3.56wt% of hydrogen at 400°C under a hydrogen pressure of 110bar. The hydrogen absorption capacity and kinetic properties of the Li–Al–N–H composite significantly improved when CeF3 was added to the composite. A maximum hydrogen absorption capacity of 4.8wt% was reached when the composite was doped with 2mol% CeF3.