316L Stainless-Steel Carburizing Close to Eutectic Transformation Using the Spark Plasma Sintering Process

Yoann Pinot,Aurélien Besnard,Maria-Rosa Ardigo-Besnard,Florian Bussière
DOI: https://doi.org/10.1007/s11665-024-09386-7
IF: 2.3
2024-03-28
Journal of Materials Engineering and Performance
Abstract:This work focuses on the 316L austenitic stainless-steel case-hardening microstructure, after the SPS process near the solid/liquid state transition temperature. This process, faster than conventional carburizing techniques, is equivalent to weld cladding, allowing the achievement of high surface carbon contents with large-size carbide grains in the case of partial melting. Three distinct zones were formed: internal carburizing, carburizing with melting, and carburizing with melting and chromium depletion; all three composed of mixed carbides (Cr 0.4 Fe 0.6 ) 7 C 3 distributed in an austenitic matrix. The internal carburizing layer growths following a parabolic kinetic law with ≈ 10 −7  cm 2 /s, while the advancement of the melting front is very fast and follows a linear law with k l = 1.0 × 10 −4  cm 2 /s at 1100 °C. The Cr-depleted fusion zone microstructure is similar to a composite material with a metallic matrix, which includes graphite particles, Mo-rich intermetallic phases, and core-shell eutectic carbides. The partial melting zone without Cr depletion shows the formation of a dense carbide layer with diameters exceeding 10 μm, constituting 60% of the volume, and achieving a hardness of 850 HV 5 . Its wear rate is about 100 times lower than the 316L steel, indicating a significant improvement in the alloy's wear behavior.
materials science, multidisciplinary
What problem does this paper attempt to address?