Mechanical Properties and Formation Mechanism of Surface Hard Nanocrystalline Carbon Diffusion Layer on 18Cr2Ni4WA Steel Induced by Supersonic Fine Particle Bombarding

Jinna Liu,Xiufang Cui,Yanbo Chen,Guo Jin,Zuo Wang

DOI: https://doi.org/10.1007/s11665-022-07695-3

IF: 2.3

2022-12-29

Journal of Materials Engineering and Performance

Abstract:Nanostructured carbon diffusion layers were produced on the 18Cr2Ni4WA low carbon steel using supersonic fine particles bombarding (SFPB) with activated carbon powders and low-temperature annealing at 500 °C. The microstructures and the formation mechanism of hard nanocrystalline carbon diffusion layers were analyzed by scanning electron microscopy (SEM), transmission electron microscopy (TEM) and molecular dynamics simulation. Additionally, the nano-hardness of the diffusion layer was measured by nanoindentation apparatus and the tribological properties were tested by wear tester. The results show that the thickness of the hard nano-carburized layer is about 20 μm. During SFPB treatment, high-speed Al 2 O 3 particles carrying activated carbon powder impact on the surface of 18Cr2Ni4WA steel, resulting in the formation of high-density dislocations and nano-surface structure, and a large amount of carbide precipitates at grain boundaries and internal defects. The carbon content of the steel surface increased from 0.17 to 4.2% (wt.%). After annealing treatment, the nano-hardness of the carburized layer reaches 7.6 GPa and the friction coefficient decreases to 0.63.

materials science, multidisciplinary