Thermodynamics of Phase Transformation and Microstructure Evolution of 18Cr2Ni4WA Carburized Steel during High‐Temperature Tempering

Bin Wang,Yanping He,Ye Liu,Yong Tian,Jinglin You,Raja Devesh Kumar Misra,Zhaodong Wang,Guodong Wang
DOI: https://doi.org/10.1002/srin.202000094
IF: 2.1258
2020-05-06
steel research international
Abstract:<p>The microstructural evolution and phase transformation mechanism in 18Cr2Ni4WA carburized steel during high‐temperature tempering was investigated using a thermodynamic model. The experimental results demonstrated that the retained austenite in the matrix decreased from the surface to the core, and martensite transformed from acicular to lath‐type. Furthermore, the hardness distribution of the carburized layer increased initially, and then decreased. Based on thermodynamic calculations, the driving forces for the decomposition of martensite decomposition and nucleation of cementite in martensite were larger than those for the decomposition of austenite during tempering. Furthermore, cementite preferentially precipitated in martensite. The driving force for the overall phase transformation of the decomposition of the retained austenite was negative, and the driving force for the nucleation of cementite in the low‐carbon retained austenite was positive, indicating that cementite could nucleate only in high‐carbon retained austenite. The low‐carbon retained austenite transformed into secondary martensite on cooling after the tempering process while the driving force gradually increased. The decomposition of the initial quenched martensite during the tempering process led to a decrease in the overall hardness of the carburized layer. The secondary martensite obtained from the retained austenite contributed to the increase in the surface hardness.</p><p>This article is protected by copyright. All rights reserved.</p>
metallurgy & metallurgical engineering
What problem does this paper attempt to address?