Strength of single‐phase high‐entropy carbide ceramics up to 2300°C

Lun Feng,Wei‐Ting Chen,William G. Fahrenholtz,Gregory E. Hilmas

DOI: https://doi.org/10.1111/jace.17443

IF: 4.186

2020-09-11

Journal of the American Ceramic Society

Abstract:<p>The mechanical properties of single‐phase (Hf,Zr,Ti,Ta,Nb)C high‐entropy carbide ceramics were investigated. Ceramics with relative density &gt;99% and an average grain size of 0.9±0.3 µm were produced by a two‐step process that involved carbothermal reduction at 1600°C and hot pressing at 1900°C. At room temperature, Vickers hardness was 25.0±1.0 GPa at a load of 4.9 N, Young's modulus was 450 GPa, chevron notch fracture toughness was 3.5±0.3 MPa•m^1/2, and four‐point flexural strength was 421±27 MPa. With increasing temperature, flexural strength stayed above ~400 MPa up to 1800°C, then decreased nearly linearly to 318±21 MPa at 2000°C and to 93±10 MPa at 2300°C. No significant changes in relative density or average grain size were noted after testing at elevated temperatures. The degradation of flexural strength above 1800°C was attributed to a decrease in dislocation density that was accompanied by an increase in dislocation motion. These are the first reported flexural strengths of high‐entropy carbide ceramics at elevated temperatures.</p>

materials science, ceramics