Abstract:Carbon nanotubes (CNTs) were synthesized on zirconium diboride (ZrB2) through CVD using a Ni catalyst. The influences of the synthesis temperature, time and catalyst amount on the quality and quantity of grown CNTs were studied. The catalyst content determined the temperature at which the CNTs began to grow. When the Ni catalyst content was low, the temperature at which the CNTs began to grow should be higher, and was 1050 °C for 5 wt% Ni content, but was 950 °C for 15 wt% Ni content. Meanwhile, agglomeration of metal atoms was observed if the synthesis temperature was increased until reaching the upper limit temperature for CNT synthesis, which was 1100 °C for 5 wt% and 10 wt% Ni content, but was 1000 °C for 15 wt% Ni content. Increased Ni catalyst content also led to higher catalytic activity as long as the Ni catalyst content did not exceed 15 wt%. Meanwhile, prolonged synthesis time extended the reaction time for the decomposition of C2H2, but resulted in the agglomeration of carbon atoms when the synthesis time was 150 min. The results showed that the uniform distribution of CNTs can be obtained in ZrB2 powder and there was no reaction between ZrB2 and Ni catalyst. The suitable synthesis conditions for obtained uniform size of CNTs grown with a higher degree of graphitization on ZrB2 that identified in this work were: Ni catalyst content of 10 wt%, synthesis temperature of 1050 °C, and synthesis time of 120 min.

Investigation of the parameters of carbon nanotube growth on zirconium diboride supported Ni catalyst via CVD

Study of Controlled Growth of Carbon Nanotubes in Microstructures at Low Temperature

The influences of synthesis temperature and Ni catalyst on the growth of carbon nanotubes by chemical vapor deposition

Carbon Nanotube Synthesis and Parametric Study Using CaCO3 Nanocrystals As Catalyst Support by CVD

The Role of the Catalytic Particle in the Growth of Carbon Nanotubes by Plasma Enhanced Chemical Vapor Deposition

Nanostructured Hybrid Carbon Nanotube/UltraHigh‐Temperature Ceramic Heterostructures: Microstructure Evolution and Forming Mechanism

Comparison of carbon nanotube deposition on HfB2, ZrB2, and TiB2 by chemical vapor decomposition

Temperature Selective Growth Of Carbon Nanotubes By Chemical Vapor Deposition

Effects Of The Supporting Method Of The Active Constituent Of Catalyst On The Syntheses Of Carbon Nanotube Using Cvd Method

Role of Nickel Particles in Selected Growth of Boron Carbonitride Tubular Structures

Pii: s0008-6223(02)00175-6

Effect of adding nickel to iron–alumina catalysts on the morphology of as-grown carbon nanotubes

Possible Tactics to Improve the Growth of Single-Walled Carbon Nanotubes by Chemical Vapor Deposition

Growth of Boron Nitride Nanotube Over Al-Based Active Catalyst and its Application in Thermal Management

Synthesis of carbon nanotubes with Ni/CNTs catalyst

Diameter-specific growth of single-walled carbon nanotubes using tungsten supported nickel catalysts

Synthesis of carbon nanotubes and carbon onions by CVD using a Ni/Y catalyst supported on copper

Study of Mg Powder As Catalyst Carrier for the Carbon Nanotube Growth by Cvd

Fabrication and Growth Mechanism of Carbon Nanotubes by Chemical Vapor Deposition

Growth of Boron Nitride Nanotubes from Magnesium-Based Catalysts

Synthesis Of High Quality Single-Walled Carbon Nanotubes By Cvd And Effect Of Catalyst'S Acidity-Basicity On Nanotubes Growth