Investigation of the parameters of carbon nanotube growth on zirconium diboride supported Ni catalyst via CVD
Jia Lin,Hua Jin,Xiaohong Ge,Yihang Yang,Guimei Huang,Jinhuo Wang,Fenqiang Li,Hui Li,Shuai Wang
DOI: https://doi.org/10.1016/j.diamond.2021.108347
IF: 3.806
2021-05-01
Diamond and Related Materials
Abstract:<p>Carbon nanotubes (CNTs) were synthesized on zirconium diboride (ZrB<sub>2</sub>) through CVD using a Ni catalyst. The influences of the synthesis temperature, time and catalyst amount on the quality and quantity of grown CNTs were studied. The catalyst content determined the temperature at which the CNTs began to grow. When the Ni catalyst content was low, the temperature at which the CNTs began to grow should be higher, and was 1050 °C for 5 wt% Ni content, but was 950 °C for 15 wt% Ni content. Meanwhile, agglomeration of metal atoms was observed if the synthesis temperature was increased until reaching the upper limit temperature for CNT synthesis, which was 1100 °C for 5 wt% and 10 wt% Ni content, but was 1000 °C for 15 wt% Ni content. Increased Ni catalyst content also led to higher catalytic activity as long as the Ni catalyst content did not exceed 15 wt%. Meanwhile, prolonged synthesis time extended the reaction time for the decomposition of C<sub>2</sub>H<sub>2</sub>, but resulted in the agglomeration of carbon atoms when the synthesis time was 150 min. The results showed that the uniform distribution of CNTs can be obtained in ZrB<sub>2</sub> powder and there was no reaction between ZrB<sub>2</sub> and Ni catalyst. The suitable synthesis conditions for obtained uniform size of CNTs grown with a higher degree of graphitization on ZrB<sub>2</sub> that identified in this work were: Ni catalyst content of 10 wt%, synthesis temperature of 1050 °C, and synthesis time of 120 min.</p>
materials science, multidisciplinary,physics, applied, condensed matter, coatings & films