Abstract:As the first wall candidate material in the future fusion device, Reduced Activation Ferritic/Martensitic (RAFM) steel represented by CLF-1 steel was further investigated on the deuterium (D) erosion and retention behaviours. The influences of the surface conditions, including surface morphology, W-enriched structure and the original surface roughness, of the surface conditions including the sample temperature, W-enriched structure and the original surface roughness are mainly discussed. The results showed that with the increase of the sample temperature of CLF-1 steel during D-plasma exposure, the surface morphology changed obviously, and the grooves/pits formed by the erosion on the sample surface are deepened and the boundary becomes obvious. Then, the granular nanostructures appeared at the erosion edges and covered the grooves, eventually forming the nanoclusters structure on the surface. At the same time, TEM results showed that the thickness and content of W atoms on the surface increased. Under the combined action of the above surface conditions, both the sputtering rate and total D retention amount of CLF-1 steel decrease. Under the current experimental parameters, with the increase of the initial surface roughness, the sputtering morphology and the surface roughness of CLF-1 steel changed to different degrees after erosion of D, which eventually led to the slightly increase of the sputtering rate. The effect of incident D-plasma angle on the sputtering and redeposition behaviour of the material may explain this phenomenon. Besides, both the specific surface area of the contact plasma and the erosion behaviour of the material by D-plasma increased with the original surface roughness. The D releasing peak, thermal desorption temperature and total D retention amount of CLF-1 steel samples decrease with the original roughness of CLF-1 steel, which is mainly caused by the increase of D diffusion on the surface. At present, it can be found that the W-enriched surface behaviour induced by D-plasma exposure as well as the change of roughness and morphology lead to the decrease of the sputtering rate of RAFM steel with fluence, energy and sample temperature.

Evolution of liquid lithium corrosion behavior for CLF-1 steels induced by high-flux helium irradiation

Study on Corrosion Behavior of China low activation Ferritic/martensitic Steel in Static Liquid Lithium

Erosion and Deuterium Retention of CLF-1 Steel Exposed to Deuterium Plasma

Study on the Microstructure and Properties Evolution of CuCrZr/316LN-IG Explosion Bonding for ITER First Wall Components

Preliminary Experiments on the Corrosion of CLAM Steel in Flowing Eutectic LiPb

Corrosion Experiments of the Candidate Materials for Liquid Lithium Lead Blanket of Fusion Reactor

Irradiation Damage of Reduced Activation Ferritic/martensitic Steel CLAM Exposed to Low-Energy High-Flux D + He Mixture Plasma

Influences of displacement damage due to heavy ion irradiation on deuterium retention in CLF-1 steel

Experimental study on corrosion compatibility of laser-welded ODS steel with liquid lead lithium

Helium Irradiation-Induced Segregation and Mechanical Response in China Low Activation Martensitic (CLAM) Steel

Influence of Surface Structure on D Retention and Erosion Behaviours of RAFM Steel with D-plasma Exposure

Corrosion Kinetics and Mechanisms of 15-15Ti Steel in Flowing Liquid Lead-Bismuth Eutectic at 500°C

The effect of He-induced surface microstructure on D plasma-driven permeation through RAFM steel

Deterioration of irradiation resistance of ODS-F/M steel under high concentration of helium

Dissolution corrosion of FeCrAl alloy exposed to oxygen-depleted lead-bismuth eutectic containing Ni impurities at 600 °C

Structure of surface oxides on martensitic steel under simultaneous ion irradiation and molten LBE corrosion

Effect of helium and its synergism with displacement damage on microstructure of CLAM steel investigated by single, sequential and simultaneous Fe and He ion irradiations

Preliminary experimental study of liquid lithium water interaction

Fabrication Aspects and Performance Characterization of α-Al2O3/ALPO4 Based Sandwich Configuration Flow Channel Inserts and Coatings for High Temperature Liquid Metal Applications

Wetting property of liquid Pb on different steel candidates as structural materials for the Generation IV nuclear reactors

Effect of Cryogenic Laser Surface Modification on the Microstructure Evolution and Corrosion Resistance of Accident-Tolerant FeCrAl Alloys