Abstract:Intelligent additive manufacturing is the future direction, and changing parameters during manufacturing process is an effective measure to adjust the quality of parts. In this study, the stability behavior of the manufacturing process under three process strategies, low layer thickness fabrication (LLTF), high layer thickness fabrication based on the interval of the powder layer thickness (IPLT), and changing of layer thickness strategy (CLTS), was comparatively investigated. Multilayer experiments and mechanical properties experiments were performed during laser powder bed fusion, and the correlation between manufacturing quality and powder layer thickness was compared. By optimizing the process parameters, the surface quality of CLTS is similar to that of LLTF, and the value of minimum surface roughness can be between 22 and 23 μm. Only balling effect due to spattering and a small amount of porosity were found in the cross-section of CLTS. The relative density of most of the fabricated parts is higher than 99%, and the highest relative density is up to 99.99%. IPLT has longer and thicker martensite than LLTF, and the β-grain of CLTS is also coarser than LLTF. The tensile properties of CLTS are similar to those of LLTF, and the ultimate tensile strength, yield strength and elongation of CLTS are 1205 MPa, 1107 MPa and 6.8%, respectively. Due to the anisotropy of the LPBF, the horizontally constructed Ti–6Al–4 V specimens yielded higher strengths, while the vertically constructed specimens obtained better elongation. The fracture of the part is characterized by a mixture of brittle fracture, ductile fracture and quasi-dissociative fracture. The surface quality, relative density and mechanical properties of CLTS are similar to those of LLTF, while the forming efficiency is much higher than that of LLTF, which can reach 7.35 mm3/s.Graphical abstract

Microstructures and mechanical properties of functionally graded TiCN–TaC ceramics prepared by a novel layer processing strategy

A strong, machinable, and multifunctional Ti3SiC2-(Ti3SiC2-Cf) composite: Gradient architecture and mechanical properties

Microstructure and Mechanical Properties of Ti60-Ti2alnb Functionally Graded Materials Fabricated by Laser Directed Energy Deposition

In-situ synthesis and low-temperature fabrication of B4C/TiB2-based multilayer graded composites with B4C and Ti–Al intermetallics mixtures through transient liquid phase sintering

Preparation and characterization of Al2O3–Ti3SiC2 composites and its functionally graded materials

Synthesis of Functionally Graded AA7075-B4C Composite with Multi-Level Gradient Structure

Microstructure and mechanical properties of TiC-Ni functionally graded materials by simultaneous combustion synthesis and compaction

Integrated preparation of B4C–TiB2 multilayer graded ceramics with high hardness and high toughness

Effect of layer thickness ratio on microstructure and mechanical properties of TiCN-HfN/TiCN-WC laminated ceramics

Microstructures and mechanical properties of the bilayer functionally graded WC-TiC-Ni/Co cemented carbides

Thermal Shock Behavior of a Novel TiCx–Ni3(Al,Ti)/Ni Functionally Graded Composite

Fabrication and properties of TiC/Ti3SiC2 composites and FGMs

Fabrication of two-dimensional graded Al2O3-(W, Ti)C–TiN–Ni–Mo nano-composites by two-stage sintering

Fabrication and Properties of TiC/Ti<sub>3</sub>SiC<sub>2</sub> Composites and FGMs

Microstructure and mechanical properties of Ti60–Ti 2 AlNb functionally graded materials fabricated by laser directed energy deposition

Multilayered Gradient Titanium-Matrix Composites Fabricated by Multi-Material Laser Powder Bed Fusion Using Metallized Ceramic: Forming Characteristics, Microstructure Evolution, and Multifunctional Properties

Graded microstructure and properties of TiCp/Ti6Al4V composites manufactured by laser melting deposition

Microstructure and Properties of Wcp/Cu Layered Functionally Graded Materials Prepared by Vacuum Hot-Pressed Sintering

Study on the organization and properties of Ti–6Al–4 V fabricated by laser powder bed fusion based on the thickness of the gradient layer

Effect of graded microstructure on the modulus, hardness, and strength of hot-pressed ZrB2-B4C FGM

Effects of TiB2 content and gradient structure on microstructural characterization and mechanical properties of TiB2/Al7050 composites