Abstract:Powder metallurgy generally is a preferred method to consolidate and prepare some refractory metals considering their high melting temperatures. However, sintering such materials to high density while maintaining fine grain structure is challenging, and generally require ultrahigh temperature or need to be assisted by external pressure. Especially, the preparation of nanostructured oxide dispersion strengthened (ODS) refractory metals at low temperature is more difficult because grain coarsening and densification are simultaneously hindered by the common oxide addition. Thus, it is of great sense to explore a kind of oxide that can be used as both strengthening phase and sintering accelerator. In this work, after extensive theoretical calculation and experimental observation, it is found that the accelerated sintering at low temperature can be achieved in W-HfO2 system. In the absence of external pressure or activator, this system can be rapidly densified without undesirable grain coarsening at a relative low temperature of only 1480 ˚C. Through kinetic analysis and density functional theory (DFT) calculation, it was confirmed that the intergranular HfO2 particles provide a rapid diffusion transport pathway for W atoms in support of densification at temperature of interest. As a result, this alloy exhibits a homogeneous microstructure with ∼97% relative density and ∼200 nm grain size, which renders our alloy with an ultrahigh compressive strength of ∼3 GPa, much higher than the reported values. We believe that the accelerated sintering mechanism found in our W-HfO2 system can be applicable to other refractory metals to prepare high-density nanocrystalline alloys with excellent properties.

The effects of oscillating frequency on microstructure and hardness of W‐Ni‐Fe refractory alloy sintered by hot oscillating pressure

Hot oscillatory pressure sintered W–Ni–Fe refractory alloy under different sintering pressures: Microstructures, densification behavior and properties

W‐Ni‐Fe refractory alloy sintered by hot oscillating pressure under different amplitudes

Sintering process in hot oscillatory pressure of 90W–7Ni–3Fe refractory alloy at different time

Oscillating pressure sintered W-Cu refractory alloy with high density and hardness under lower temperature

Influence of sintering temperature on microstructure and properties of 90W-10Ti alloy targets prepared by hot oscillating pressing

Microstructures and Properties of AlCoCrNiFe High-Entropy Alloy Sintered by Hot Oscillating Pressing Under Different Sintering Times

Microstructure and properties of AlCoCrNiFe high-entropy alloy sintered by hot oscillating pressing

Interplay of microstructure and mechanical properties of WC-6Co cemented carbides by hot oscillating pressing method

Accelerated sintering of high-performance oxide dispersion strengthened alloy at low temperature

Sintering behavior of alumina whisker reinforced zirconia ceramics in hot oscillatory pressing

Microstructure and Mechanical Properties of ZTA Composites Fabricated by Oscillatory Pressure Sintering

Hot oscillatory pressure preparing low-cost FGH4096 superalloys with high performance

Oscillatory pressure sintering of binderless tungsten carbide

Sintering behavior and mechanical properties of β-SiC ceramics under oscillatory pressure

Optimum Sintering Temperature of High Quality Silicon Nitride Ceramics under Oscillatory Pressure

Effect Of Sintering Temperature On Structures And Properties Of High Quality Zirconia Ceramics Under Oscillatory Pressure

Characteristics of 14Cr-ODS ferritic alloy fabricated by mechanically alloying and microwave sintering

Effects of Laser Oscillation Frequency on the Microstructure and Properties of TiC/Fe‐Based Alloy Composite Coatings

Effect of Oscillatory Pressure on the Sintering Behavior of ZrO2 Ceramic

W-Ti refractory alloy with high hardness forged using dynamic pressure-assisted hot pressing