Abstract:In this study, the Ni-TiO 2 coatings were deposited on copper substrates by pulse plating. The effect of multi-step current cycles on the metallurgical properties of produced coatings was investigated. The results showed that the values of applied currents within the periods significantly affect the surface properties of all coatings. Using the negative current cycles, the surface morphologies completely changed from regular and compact to irregular, compared to the deposits that did not have a negative cycle in the coating process. Also, the surface roughness increased by 1.5 times in the best case. Applying the 8-step cycle increased the percentage of TiO 2 content inside the Ni-TiO 2 layer from 13.13 vol.% to 31.58%. The corrosion and wear analysis results showed that the coating applied by a 4-step cycle with a 90-second off time has the best properties. Therefore, the corrosion and wear properties were not necessarily directly related to the participation percentage of TiO 2 particles. Compact morphology with high current efficiency, wide distribution of TiO 2 particles (6.31 vol.%) with minimal agglomeration, low coating roughness (R a = 0.32 μm), high hardness value (436 Vickers), and the participation of (111) plane in the preferred texture improved the corrosion and wear behaviour of the optimal coating. Dans cette étude, on a déposé des revêtements composites de Ni-TiO 2 sur des substrats de cuivre par la méthode de placage pulsé. On a examiné l'effet de cycles de courants pulsés à plusieurs étapes sur la morphologie de la surface, la teneur en TiO 2 , l'usure et les propriétés de corrosion des revêtements produits. Les résultats ont montré que les valeurs des courants appliqués dans les périodes avaient un effet significatif sur les propriétés de surface de tous les revêtements. En utilisant les cycles de courant négatif pour tous les échantillons, les morphologies de surface étaient complètement modifiées par rapport aux dépôts qui n'ont pas eu de cycle négatif dans le procédé de revêtement. Dans ces échantillons, la morphologie a changé d'une forme régulière et compacte à une forme irrégulière. Également, la rugosité de la surface a augmenté de 1.5 fois dans le meilleur des cas. Appliquer le cycle à 8 étapes a même augmenté le pourcentage de la teneur en TiO 2 dans la couche de Ni-TiO 2 de 13.13% à 31.58% en volume. Les résultats de l'analyse de corrosion et d'usure ont montré que le revêtement appliqué par un cycle à 4 étapes avec un temps d'arrêt de 90 secondes possédait les meilleures propriétés. Par conséquent, les propriétés de corrosion et d'usure n'étaient pas nécessairement reliées directement au pourcentage de participation des particules de TiO 2 dans la couche de matrice de nickel. Une morphologie compacte avec une efficacité de courant élevée (98%), une grande distribution de particules de TiO 2 (6.31% en volume) avec une agglomération minimale, une faible rugosité du revêtement (R a = 0.32 μm), une valeur de dureté élevée (436 Vickers) et une participation du plan (111) dans la texture préférée ont amélioré le comportement à la corrosion et à l'usure du revêtement optimal.

The effect of positive and reverse current cycles on the wettability, morphology, and corrosion behaviour of electrodeposited nickel matrix layer

The effect of multi-step cycles on the surface properties of Ni-TiO2 coatings produced by pulse current electrodeposition

The Influence of Pulse Plating Parameters on the Structure and Corrosion Behavior of Ni-W-TiC Nanocomposite Coatings

Effect of Pulse Electrodeposition Mode on Microstructures and Properties of Ni-TiN Composite Coatings

Corrosion Studies on Pulse Reverse Ni-Mo Coatings Electrodeposited on Cu Substrate

Study of the Effect of Current Density on the Metallurgical Properties of AlFeCrNiTi High Entropy Alloy Coating Produced by Pulse Plating

Effects of Direct and Pulse Plating on the Co-Deposition of Sn–Ni/TiO2 Composite Coatings

Effect of Current Density and Bath Temperature to The Corrosion and Wear Behaviour of Tungsten Carbide - Nickel Electrodeposition Coating

Effect of Electrolyte pH on Microstructure, Corrosion Behavior, and Mechanical Behavior of Ni-P-W-TiO2 Electroplated Coatings

Characterization of Co–Cr–Fe–Mn–Ni High-Entropy Alloy Thin Films Synthesized by Pulse Electrodeposition: Part 2: Effect of Pulse Electrodeposition Parameters on the Wettability and Corrosion Resistance

Corrosion behavior of TiN and TiCN coatings synthesized by PVD on the spark plasma sintered NiTi substrate

Preparation of Ni-TiO2 Composite Coatings on Q390E Steel by Pulse Electrodeposition and their Photocatalytic and Corrosion Resistance Properties

Surface Characterization and Electrochemical Studies of Biomedical Niti Alloy Coated with Tin by Piiid

Effects of substrate materials and electrodeposition parameters on hydrogen evolution reaction of Ni–Cu–Fe coatings

A promising perspective in improving corrosion and wear resistance of plain steel through electrodeposition of thick Ni–Mo–W ternary alloy

Electrochemical Corrosion Behavior of Ni–TiO2 Composite Coatings Electrodeposited from a Deep Eutectic Solvent-Based Electrolyte

Electrochemical behavior and electro-crystallization mechanism of Cu-Ni/Nano-Al 2 O 3 coating with a deposition current density dependence

Studies on Pitting Corrosion of Pulsed Electrodeposited Nanocomposite Coating

Fabrication and characterization of Ni-TiO 2 and Ni-V 2 O 5 single-layer and double-layer coatings with the approach of improving the wear and corrosion properties

Influence of processing parameters on final characteristics of Ni-P-MWCNT coatings produced by pulsed electrodeposition

Preparation and Investigation of Ni–Co–P Alloy Coatings Using Jet Electrodeposition with Varying Pulse Parameters