Fabrication and characterization of Ni-TiO 2 and Ni-V 2 O 5 single-layer and double-layer coatings with the approach of improving the wear and corrosion properties

Ali Hadipour,Mohammad Reza Hosseini,Mohammad Ebrahim Bahrololoom

DOI: https://doi.org/10.1016/j.surfcoat.2024.130580

IF: 4.865

2024-02-24

Surface and Coatings Technology

Abstract:The main purpose of this study is to investigate the metallurgical behavior of Ni-TiO 2 and Ni-V 2 O 5 single-layer coatings and compare them with Ni-TiO 2 /Ni-V 2 O 5 and Ni-V 2 O 5 /Ni-TiO 2 double-layer coatings. The general attitude is the optimal choice of coatings in terms of wear and corrosion properties. The dimensions of TiO 2 and V 2 O 5 ceramic powders were 20 nm and 500 nm, respectively, and their morphology was also different. The presence of the submicron V 2 O 5 particles was more than the TiO 2 nanoparticles in the nickel matrix deposit. Also, with double layering the coatings (Ni-TiO 2 /Ni-V 2 O 5 and Ni-V 2 O 5 /Ni-TiO 2 ), the presence of ceramic particles in the upper layer had increased compared to the same single-layer coatings. Therefore, the increase in the hardness of the deposits was directly related to the percentage of ceramic powders in the coating. The surface morphology of the Ni-TiO 2 layers was formed as a cauliflower shape while the Ni-V 2 O 5 deposits had a smooth morphology. Increasing participation of TiO 2 particles in the Ni-TiO 2 layer had made the morphology rougher. Also, by applying the Ni-TiO 2 layer under the Ni-V 2 O 5 deposit, the surface morphology of the Ni-V 2 O 5 layer became smooth, which can be due to the increase in the V 2 O 5 content in this layer. The lowest amount of fluctuation appeared in the roughness profiles related to the Ni-V 2 O 5 layers, and the large fluctuation range in the Ni-TiO 2 layers was due to the smooth and cauliflower structure, respectively. The crystallite size in double-layer coatings was smaller than the single-layer coatings due to the higher nucleation and growth rate of nickel deposition in the nickel matrix upper layers. According to the presented results, the Ni-V 2 O 5 and Ni-V 2 O 5 /Ni-TiO 2 coatings were the most wear resistant coatings. Also, the Ni-V 2 O 5 /Ni-TiO 2 and Ni-TiO 2 /Ni-V 2 O 5 double-layer coatings were suitable candidates for corrosion resistance and to consider both properties, Ni-V 2 O 5 /Ni-TiO 2 was very suitable. Hardness, surface morphology, roughness, preferred planar texture, and ceramics powder participation were important parameters in determining the wear and corrosion properties of coatings. Also, it seems that the effect of the double layering of nickel matrix deposits on the metallurgical properties was greater than the dimensions of the ceramic particles participating in the coating.

physics, applied,materials science, coatings & films