Abstract:Barium titanate powder with average particle size near 300 nm was produced using the low-temperature synthesis. It was established using scanning electron microscopy that at the thermal treatment, the particles gradually decrease with the formation of polydisperse aggregates. Based on the thermogravimetric analysis of the synthesized powder held in air for 4 months, it was shown that along with the low-temperature phase, the sample contains a high-temperature phase of carbonates, which removes at ~ 900 °C. Sorption characteristics of barium titanate thermally treated at various temperatures were obtained from the results of adsorption-desorption of nitrogen vapors. The specific surface area of the BaTiO3 powder was 76 m2/g. It was found that further heat treatment leads to a decrease in the specific surface area. The X-ray diffraction analysis of barium hydroxotitanil annealed at temperatures from 120 °C to 800 °C showed that the thermal treatment of the sample leads to the formation of a completely formed phase of barium titanate. The DSC temperature was used to determine the Curie temperatures for a HTB powder thermally treated in the temperature range from 120 to 800 °C. Dielectric spectra of suspensions of the synthesized powder were obtained during the heat treatment. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . .

Low-temperature Synthesis of Highly Dispersed Barium Aluminate

Low-Temperature Synthesis of Highly Dispersed Calcium Aluminate

LOW-TEMPERATURE SYNTHESIS OF BARIUM TITANITE IN AQUEOUS SOLUTION

Synthesis of Highly Dispersed Barium Titanate Nanoparticles by a Novel Solvothermal Method

Low-temperature Synthesis and Analysis of Barium Titanate Nanoparticles with Excess Barium

Low-temperature synthesis of barium titanate thin films by nanoparticles electrophoretic deposition

Room-Temperature Synthesis of BaTiO<sub>3</sub>Nanoparticles in Large Batches

Synthesis and Processing of Barium Hexaaluminogallates

Low-temperature synthesis of barium titanate in the mesoporous polyethylene matrices

Low-Temperature Synthesis and Characterization of AlPO-Cristobalite in Ionic Liquid

Low temperature preparation of strontium barium niobate powders from metal carboxylate gels

Low-temperature combustion synthesis of nanometer tetragonal barium titanate powders

Structure and emission properties of barium calcium aluminates synthesized by room-temperature solid-state reaction approach

Specifics of Obtaining a Vacuum-Tight Weakly Conductive Ceramics Based on Barium Aluminate

A Study on Low Temperature Synthesis of BaTiO3

Low-Temperature Synthesis of Barium Titanate in a Mesoporous Polyethylene Matrix

A novel method for the synthesis of nano-sized BaAl2O4 with thermal stability

Synthesis and Characterization of a New Layered Barium Aluminate Containing Six-Membered Rings: BaAl2O3(OH)2·H2O

Low-temperature Preparation of Pure BaTiO_(3) by SAG Method

Synthesis of monodispersed barium titanate nanoparticles with narrow size distribution by a modified alkoxide-hydroxide sol-precipitation method

Low-temperature Combustion Synthesis and Characterization of Nanosized Tetragonal Barium Titanate Powders