Inhibitory effect of La 3+ on hydrogen damage of 27CrMo44S/1 steel in H 2 S-containing acidic solution

Zhengyi Xu,Hao Liu,Donatien Ngendabanyikwa,Bing Lei,Zhiyuan Feng,Junyi Wang,Yawei Shao,Guozhe Meng,Yanqiu Wang,Fuhui Wang

DOI: https://doi.org/10.1016/j.jmrt.2023.06.267

IF: 6.267

2023-07-13

Journal of Materials Research and Technology

Abstract:The effect of La 3+ on the hydrogen permeation behavior of 27CrMo44S/1 steel in acidic environments containing H 2 S is investigated through the measurement of steady-state permeation current density ( i ∞ ), hydrogen diffusivity ( D ), and subsurface hydrogen concentration ( C 0 ). Results indicate that the addition of La 3+ can remarkably reduce i ∞ . The corrosion products with La 3+ involved in the film formation process in the H 2 S-free environment have a good hydrogen barrier effect, but the addition of La 3+ hardly influence the D value of 27CrMo44S/1 steel in the H 2 S-containing environment. However, the presence of La 3+ substantially reduces the C 0 on metal surface regardless of the presence of H 2 S in the solution. Static immersion and tensile experiments illustrate that the addition of La 3+ can improve the corrosion resistence and plasticity loss of the material in the H 2 S environment.

materials science, multidisciplinary,metallurgy & metallurgical engineering