Effect of La content on inclusion morphology in automobile sulfur‐containing gear steel SCr420H

Meng Sun,Zhouhua Jiang,Yang Li,Changyong Chen,Yunqie Mao,Shuai Ma,Yucheng Wang,Hang Liu

DOI: https://doi.org/10.1002/srin.202300127

IF: 2.1258

2023-05-27

steel research international

Abstract:The inclusion morphology of sulfur‐containing gear steel with different La addition (0, 0.08, 0.5, and 1%) was investigated in laboratory experiments. The La and S concentrations in steel melt significantly decreased with the holding time after La addition increased, leading to different types of inclusions with specific shapes. Inclusion transformation routes with the holding time increased under different La addition were summarized as follows: (i) 0%La addition: cluster‐like Al2O3 + cluster‐like MnS → irregular block‐like MgAl2O4 + cluster‐like MnS. (ii) 0.08%La addition: cluster‐like LaAlO3 + spherical‐like La‐Al‐O‐S‐(MnS) → spherical‐like La‐Al‐O‐S‐(MnS) + spherical‐like La‐Al‐O‐S‐(MgO)‐(MnS) + cluster‐like MnS. (iii) 0.5%La addition: flower‐like La‐O + spherical‐like La‐O‐S → spherical‐like La‐O‐S. (iv) 1%La addition: flower‐like La‐O + spherical‐like La‐O‐S → spherical‐like La‐O‐S + cubic‐like La‐O‐S‐N‐As. The results of hot compression suggest that La‐containing inclusions are less prone to the shape change than MnS; moreover, microcracks formed at the surface of La‐containing inclusions. The nanoindentation test demonstrates that the hardness of La‐O‐S is higher than MnS. The high La addition has a remarkable effect on refractory degradation. For 0.5% and 1% La, dissolved La reacted with the MgAl2O4 phase in the MgO‐MgAl2O4 dual‐phase refractory and changed into LaAlO3. This article is protected by copyright. All rights reserved.

metallurgy & metallurgical engineering