Abstract:Ultrafine binderless WC-based cemented carbides with varied amounts of AlN nano-powder (0–16wt.%) were fabricated by spark plasma sintering at 1600°C under a pressure of 50MPa with the assistance of VC and TaC as WC grain growth inhibitors. The densification behavior, phase composition, microstructure and mechanical properties of the as-prepared samples were investigated. During sintering, rapid sample shrinkage started at about 1050°C and ended at about 1550°C. X-ray diffraction analysis revealed that an appropriate addition amount of AlN nano-powder would be of help to limit the formation of W2C phase and promote the formation of solid solution phase of (V,W)C2 during sintering. As the added fraction of AlN nano-powder increased, the relative density of the samples initially increased and then decreased, reaching its maximum of about 99.6% when 3–5wt.% AlN nano-powder was added. Scanning electron microscopy examination indicated that the average size of WC grains in the samples was about 0.7μm and with increasing added fraction of AlN nano-powder, the abnormal growth of WC grains was suppressed and their sizes were somewhat reduced. Both the sample hardness and flexural strength first increased and then decreased with increasing added fraction of AlN nano-powder, reaching the maximum hardness of about 2400 HV10 with 3wt.% AlN nano-powder and maximum flexural strength of about 1250MPa with 5wt.% AlN nano-powder, respectively. However, the fracture toughness slightly decreased from 7.5 to 6.3MPa·m1/2 with increasing added fraction of AlN nano-powder.

Influence of Nano-Sized La2O3 Addition on the Sintering Behavior and Mechanical Properties of WC–La2O3 Composites

Influences of Ni/Cu/Cr3C2 Composite Additive on Microstructure and Properties of WC–10Co Fine Grained Hardmetal

Influence of La2O3 Addition on Hardness, Flexural Strength and Microstructure of Hot-Pressing Sintered WC–MgO Bulk Composites

Effect of La2O3 content on the densification, microstructure and mechanical property of W-La2O3 alloy via pressureless sintering

Effect of ZrC nano-powder addition on the microstructure and mechanical properties of binderless tungsten carbide fabricated by spark plasma sintering

Effect of Nano-AlN Addition on the Microstructure and Mechanical Properties of Binderless WC-VC-TaC-AlN Cemented Carbides

Ultrafine grained WC-10FeCoCu cemented carbides doped with La 2 O 3 prepared by spark plasma sintering

Ultrafine Binderless WC-based Cemented Carbides with Varied Amounts of AlN Nano-Powder Fabricated by Spark Plasma Sintering

Microstructure and Properties of La2O3 Doped W Composites Prepared by a Wet Chemical Process

Improved comprehensive mechanical properties of oscillatory pressure sintered WC–ZrO2–Al2O3 ceramics with VC/Cr3C2 addition

Selective laser melting of lanthanum oxide-reinforced tungsten composites: microstructure and mechanical properties

Microstructures and Properties of W-Lu2O3 Composites Strengthened with Nb and C Trace Elements

Effect of SiC Nano-Whisker Addition on WC–Ni Based Cemented Carbides Fabricated by Hot-Press Sintering

Effect of La2O3 addition on wear properties of Ni60a/SiC coating using laser-cladding

Effect of La203 Addition on Microstructure and Microwave Dielectric Properties of A]203 Ceramics

Microstructure and mechanical properties of pressure‐less sintered B4C–SiC–ZrB2–LaB6 ceramic composites

Effects of La on microstructure and mechanical properties of NbMoTiVSi0.2 refractory high entropy alloys

Microstructure Evolution and Hardness Improvement of WC-Co Composites Sintered with Fe Substituting Part of Co Binder

Study on forming process and performance of nano-La 2 O 3 reinforced tungsten-based composites by selective laser melting

Effects of nano-alumina on mechanical properties and wear resistance of WC-8Co cemented carbide by spark plasma sintering

Microstructure and mechanical properties of oscillatory pressure sintered WC ceramics with different carbon sources