Abstract:The influence of Mo (10‐40at.%) additions to Cr‐8at.%Si was systematically studied by producing arc melted alloys and analyzing the as‐cast and annealed microstructures as well as the oxidation resistances. The majority of the alloys contained a solid solution A2 matrix with the intermetallic A15 = (Cr,Mo)3Si phase. The oxidation resistance was tested by thermogravimetric analysis (TGA) at 1200 °C in air for 50 and 100 h. Samples were characterized by XRD, SEM and EPMA (WDS). The studied Cr‐xMo‐8Si alloy series showed a beneficial effect of Mo on the corrosion behavior of the annealed arc melted alloys exposed at 1200 °C in air. An increased amount of A15 led to the formation of a continuous SiO2 scale beneath the Cr2O3 layer during high temperature exposure. The internal SiO2 layer inhibited further internal oxidation of the A15 phase. Prior annealing also influenced the oxidation behavior of the alloys. Higher annealing temperatures, resulted in an overall reduced fraction of the A15 phase, as well as coarsening, but also showed a more uniform size and distribution of the precipitates, which seems to benefit the formation of a protective duplex oxide scale. Cr‐25Mo‐8at.%Si annealed at 1350 °C for 100 h, showed the most promising oxidation behavior after exposure in air at 1200 °C for 100 h. For all of the investigated Mo contents, no nitridation was observed when compared to the Cr‐8Si reference composition. The oxide scale adhesion also was improved. For Mo >25 at.% no spallation was observed. Evaluation of the TGA data showed it follows the paralinear law, with both the growth rate, kp, and volatilization rate, kv, of Cr2O3 being reduced by adding 10‐25 at.% Mo. A binary Cr/Mo‐Si phase diagram was generated for the studied alloy series in order to determine accurate annealing conditions and estimate the stability range of the metastable σ phase. This article is protected by copyright. All rights reserved.

THE INFLUENCE OF Mo‐CONTENT AND ANNEALING ON THE OXIDATION BEHAVIOUR OF ARC‐MELTED Cr‐xMo‐8Si ALLOYS

Effect of Mo Content on Microstructure and Properties of 00cr12ni9mo (x) Cu2Ti Maraging Stainless Steel

Effect of microalloying with silicon on high temperature oxidation resistance of novel refractory high-entropy alloy Ta-Mo-Cr-Ti-Al

The Effects of Alloying Elements Cr, Al, and Si on Oxidation Behaviors of Ni-Based Superalloys

High-temperature steam oxidation behavior of an FeCrAl alloy with controlled addition of Mo

Microstructure, mechanical properties and tribocorrosion characteristics of (Mo1-xCrx)5Si3 alloys

Effect of Si solution in α-Mo on oxidation behavior of Mo-Si-B alloy and oxidation kinetics model

Influence of TiC contents on the microstructure, mechanical properties, and oxidation behavior of Mo–10Si–8B alloys

Oxidation Behavior of the Si-B-X (X = Mo, Cr, or Ti) Alloys in the Temperature Range of 1000–1400 °C

Study on the high-temperature oxidation of AlCrFeCoNi-based high-entropy alloys with trace Si additions

Preparation and enhanced oxidation behavior of microalloyed Mo5SiB2 alloy at 1300 °C

Effect of Mo on the high-temperature oxidation behavior of Cr-Ni-Mo Hot-Work Die Steels

Oxidation and Hot Gas Corrosion of Al–Cr–Fe–Ni‐Based High‐Entropy Alloys with Addition of Co and Mo

Study on the Pre-Oxidation and Resulting Oxidation Mechanism and Kinetics of Mo-9Si-8B Alloy

Effect of Molybdenum on Isothermal Oxidation Behavior of 4th Generation Nickel-Based Single Crystal Superalloys

Control of High-Temperature Static and Transient Thermomechanical Behavior of SiMo Ductile Iron by Al Alloying

Oxidation Behavior of (Mo,Hf)Si2-Al2O3 Coating on Mo-Based Alloy at Elevated Temperature

Oxidation behavior and high-temperature tensile properties of Fe-9Cr-(Mo, Mo/Ni) alloys

Microstructure refinement and oxidation behavior improvement in Mo modified TiAl4822 alloy prepared by vacuum sintering

High Temperature Oxidation Performance of an Additively Manufactured Mo–9Si–8B Alloy

Enhancing oxidation resistance with Si in Fe36Ni36Al15Cr10Si2Mo1 multi-principal element alloy at 700 °C