Abstract:Self-stressing steel tube concrete is a novel composite structure created by substituting ordinary concrete with self-stressing expansion concrete within a steel tube. Compared to regular steel tube concrete, self-stressing steel tube concrete structures can overcome the limitation that ordinary steel tube concrete is prone to voids. Many engineering studies have shown that these structures are prone to fatigue damage at the welded joints of steel tubes under repeated loads. Factors such as welding residual stress, welding defects, and stress concentration contribute to this susceptibility, which could potentially lead to catastrophic accidents. In this study, fatigue tests and finite element analysis were conducted on self-stressed concrete-filled steel tube joints of DY-type joints. The fatigue behavior of the joints under alternating loads was investigated through experiments and validated with the finite element analysis results. The impact of concrete's self-stress on joint fatigue performance was examined, including the stress concentration factor (SCF) and geometric parameters such as the ratio of the branch pipe outer diameter to the main pipe outer diameter, the ratio of the main pipe's outer radius to its wall thickness, the ratio of the branch pipe wall thickness to the main pipe, and the correlation between the angle of the main pipe and the branch pipe. The research results show that the node can withstand 2 million alternating loads without failure under a fatigue stress amplitude of 47.2 MPa. Additionally, the fatigue life of the test model under variable amplitude loads is converted into that under constant amplitude loads. The fatigue life of the node indicates that it can withstand 4.16 million cycles under the given fatigue amplitude before fatigue cracks appear. Additionally, variations in geometric parameters can impact the fatigue life of the node, but do not lead to changes in the initiation position of fatigue cracks. Moreover, as self-stress increases, the fatigue performance of the tube node will decrease, although the effect of self-stress on the stress distribution around the weld is minimal.

Internal stud node of steel pipe concrete truss structure and construction method thereof

Steel Pipe Node Test of the 500 Kv Hanjiang River Crossing Tower Steel

Comparison Study on Stability Behavior Between Steel Pipe Arch Bridge and CFST Truss Arch Bridge

STUDY ON APPLICATION OF CONCRETE FILLED PRESTRESSING STEEL TUBULAR STRUCTURE

EXPERIMENTAL RESEARCH AND FINITE ELEMENT ANALYSIS ON A WELDED JOINT WITH TUBES INTERSECTED AT TWO DIFFERENT POINTS

Experimental study of the static behavior of tubular N-joints

Rectangular steel pipe column and I-steel beam sleeve steel plate bolt connecting node

Rigid connection node of concrete-filled tubular column and reinforced concrete beam

Reinforced steel pipe column and H-shaped beam connection node

02.05: Design of concrete-filled steel tubular longitudinal gusset plate connections

Study Of Mechanical Performance Of Concrete-Filled Steel Tubular Joints

Research on Reinforced Concrete Beam-Steel Tube Concrete Column Node

Steel-concrete combination section structure of steel main tower or steel main arch

Experimental Investigation of Concrete-Filled Steel Tubular Longitudinal Gusset Plate Connections

Bending Strength of Connection Joints of Prestressed Reinforced Concrete Pipe Piles

A numerical analysis on bending capacity of steel pipe columns using a mechanical joint with concrete-filled steel tube

Steel-concrete joint section structure of beams

The Fatigue Performance of DY-type Joints in Self-Stressed Concrete-Filled Steel Tubes

Effect of vibration on the interface properties of welded steel joints and filled concrete in steel pipes

Study on Mechanical Properties of Concrete-Filled Steel Tubular Members under Axial Tension

Design Method of the Headed Stud Embedded at the Pinned Joint of Steel Beam to Concrete Wall