Abstract:Abstract The objective of this study was to produce composites with a uniform distribution of aluminum nitride (AlN) reinforcing particles in the magnesium (Mg) metal matrix composites. In this study, experiments were carried out to evaluate the effect of time and temperature on the nitridation of aluminum to form AlN and its distribution in Mg composites. High-temperature production of AlN in Mg alloys melts using the ammonia gas bubbling method was investigated. The effect of ammonia bubbling time and temperature at a flow rate of 0.1 liters per minute on the amount of AlN formation was studied. Bubbling of ammonia gas resulted in the in-situ formation of AlN in Mg alloys, yielding AlN-reinforced Mg alloy composites. The AlN formation in the alloy was increased with increasing bubbling time. The rate of AlN formation was found to be 0.34 g·min −1 at 1,073 K. An average yield of AlN (wt%) was 6.47, 29.65, and 27.43 at 973, 1,073, and 1,173 K, respectively. An activation energy of 59.57 kJ was determined for the nitridation process. The magnitude of activation energy indicates that the reaction proceeds in the mixed regime with control of both nucleation and interface diffusion. The product was characterized using X-ray diffraction (XRD), optical microscopy, and scanning electron microscopy. The characterization of samples showed that the AlN particles distributed throughout the alloy matrix. The AlN particles formed in-situ are small in size, and uniform dispersion of AlN particles was observed at higher bubbling times and at higher temperatures. The AlN crystallite size increased with an increase in bubbling time and temperature. The XRD characterization results showed that the composite formed in-situ was composed of (Mg), intermetallic γ-(Mg, Al), and AlN phases. The Rockwell hardness of the in-situ composites was higher than the un-reinforced Mg alloy, and the hardness increased with an increase in the AlN wt% in the Mg alloy composites.

Interaction of Al2O3 Melt with Nitrogen at High Temperatures and Pressure of 1 Bar

Mass transfer in the Earth’s interior: fluid-melt interaction in aluminosilicate–C–O–H–N systems at high pressure and temperature under oxidizing conditions

High-temperature behaviour of V2AlC powders under nitrogen atmosphere

Reactions of Laser-Ablated Aluminum Atoms with Nitrogen Atoms and Molecules. Infrared Spectra and Density Functional Calculations for the AlN2, Al2N, Al2N2, AlN3, and Al3N Molecules

Disruption of an Alumina Layer During Sintering of Aluminium in Nitrogen

Investigation on the Microstructure and High-Temperature Properties of AlN Coating Through Oxygen Addition

Thermal stability and selective nitridation of Cr2AlC in nitrogen at elevated temperatures

Chemical compatibility of a TiAl-Nb melt with oxygen-free crucible ceramics made of aluminum nitride

Reaction Synthesis of Aluminum Nitride-Boron Nitride Composites Based on the Nitridation of Aluminum Boride

Secondary Phases and Interfaces in a Nitrogen-Atmosphere Sintered Al Alloy: Transmission Electron Microscopy Evidence for the Formation of AlN During Liquid Phase Sintering

High-temperature production of AlN in Mg alloys with ammonia gas

Synthesis of aluminum nitride by nitridation of γ-Al 2O3 nanopartlcles in flowing ammonia

Mechanism of carbothermal synthesis of aluminium nitride

Reactions of Laser-Ablated Aluminum Atoms with Nitrogen During Condensation at 10 K. Infrared Spectra and Density Functional Calculations for AlxNy Molecular Species

Synthesis of Aluminum Nitride by Nitridation of γ-Al<sub>2</sub>O<sub>3</sub> Nanoparticles in Flowing Ammonia

Formation and properties of rocksalt-type AlN and implications for high pressure phase relations in the system Si–Al–O–N

Reactive phase behavior of aluminum nitrate in high temperature and supercritical water

In situ reaction mechanism of MgAlON in Al–Al2O3–MgO composites at 1700°C under flowing N2

Solubility of nitrogen and inclusion characteristics in high aluminium steels

Thermodynamics of the Interaction of Niobium and Tantalum with Oxygen and Nitrogen at Temperatures near the Melting Point